Method for Manufacturing Photocatalytic Porous Concrete
The present invention relates to a method of manufacturing photocatalytic porous concrete which is very easy to manufacture and has excellent nitrogen oxide removal performance by uniformly impregnating a photocatalyst without reducing porosity of bottom ash. The method of manufacturing photocatalytic porous concrete according to the present invention may comprise: a step (S1) of preparing a titanium dioxide (TiO_2) aqueous solution by adding a titanium dioxide (TiO_2) powder and water to a mixer and mixing the same; a step (S2) of immersing and stirring bottom ash aggregate in the titanium dioxide (TiO_2) aqueous solution; a step (S3) of maintaining the bottom ash aggregate immersed in the titanium dioxide (TiO_2) aqueous solution for a certain period of time so that titanium dioxide (TiO_2) is absorbed into a porous surface of the bottom ash aggregate; a step (S4) of removing water from the titanium dioxide (TiO_2) aqueous solution and leaving only the bottom ash aggregate impregnated with titanium dioxide (TiO_2); and a step of (S5) mixing the bottom ash aggregate impregnated with titanium dioxide (TiO_2) with a binding material and water to produce porous concrete. Accordingly, the photocatalytic porous concrete according to the present invention has excellent nitrogen oxide removal effect and also has excellent sound absorption performance and compressive strength.
본 발명은 제조가 매우 용이하며, 광촉매가 바텀애쉬의 다공성을 감소시키지 않으면서 균일하게 함침되어 우수한 질소산화물 제거 성능을 갖는 광촉매 포러스 콘크리트의 제조 방법에 관한 것으로, 본 발명에 따른 광촉매 포러스 콘크리트의 제조 방법은, (S1) 혼합기에 이산화티타늄(TiO2) 분말과 물을 투입하고 혼합하여 이산화티타늄(TiO2) 수용액을 제조하는 단계; (S2) 상기 이산화티타늄(TiO2) 수용액에 바텀애쉬 골재를 침지시키고 교반하는 단계; (S3) 상기 바텀애쉬 골재가 이산화티타늄(TiO2) 수용액 내에 침지된 상태로 일정 시간 동안 유지하여 이산화티타늄(TiO2)이 바텀애쉬 골재의 다공질 표면 내부로 흡수되도록 하는 단계; (S4) 이산화티타늄(TiO2) 수용액의 물을 제거하고, 이산화티타늄(TiO2)이 함침된 바텀애쉬 골재만 남기는 단계; 및, (S5) 상기 이산화티나늄(TiO2)이 함침된 바텀애쉬 골재를 결합재 및 물과 혼합하여 포러스 콘크리트를 제조하는 단계;를 포함할 수 있다.
Method for Manufacturing Photocatalytic Porous Concrete
The present invention relates to a method of manufacturing photocatalytic porous concrete which is very easy to manufacture and has excellent nitrogen oxide removal performance by uniformly impregnating a photocatalyst without reducing porosity of bottom ash. The method of manufacturing photocatalytic porous concrete according to the present invention may comprise: a step (S1) of preparing a titanium dioxide (TiO_2) aqueous solution by adding a titanium dioxide (TiO_2) powder and water to a mixer and mixing the same; a step (S2) of immersing and stirring bottom ash aggregate in the titanium dioxide (TiO_2) aqueous solution; a step (S3) of maintaining the bottom ash aggregate immersed in the titanium dioxide (TiO_2) aqueous solution for a certain period of time so that titanium dioxide (TiO_2) is absorbed into a porous surface of the bottom ash aggregate; a step (S4) of removing water from the titanium dioxide (TiO_2) aqueous solution and leaving only the bottom ash aggregate impregnated with titanium dioxide (TiO_2); and a step of (S5) mixing the bottom ash aggregate impregnated with titanium dioxide (TiO_2) with a binding material and water to produce porous concrete. Accordingly, the photocatalytic porous concrete according to the present invention has excellent nitrogen oxide removal effect and also has excellent sound absorption performance and compressive strength.
본 발명은 제조가 매우 용이하며, 광촉매가 바텀애쉬의 다공성을 감소시키지 않으면서 균일하게 함침되어 우수한 질소산화물 제거 성능을 갖는 광촉매 포러스 콘크리트의 제조 방법에 관한 것으로, 본 발명에 따른 광촉매 포러스 콘크리트의 제조 방법은, (S1) 혼합기에 이산화티타늄(TiO2) 분말과 물을 투입하고 혼합하여 이산화티타늄(TiO2) 수용액을 제조하는 단계; (S2) 상기 이산화티타늄(TiO2) 수용액에 바텀애쉬 골재를 침지시키고 교반하는 단계; (S3) 상기 바텀애쉬 골재가 이산화티타늄(TiO2) 수용액 내에 침지된 상태로 일정 시간 동안 유지하여 이산화티타늄(TiO2)이 바텀애쉬 골재의 다공질 표면 내부로 흡수되도록 하는 단계; (S4) 이산화티타늄(TiO2) 수용액의 물을 제거하고, 이산화티타늄(TiO2)이 함침된 바텀애쉬 골재만 남기는 단계; 및, (S5) 상기 이산화티나늄(TiO2)이 함침된 바텀애쉬 골재를 결합재 및 물과 혼합하여 포러스 콘크리트를 제조하는 단계;를 포함할 수 있다.
Method for Manufacturing Photocatalytic Porous Concrete
질소산화물 제거 성능을 갖는 광촉매 포러스 콘크리트의 제조 방법