QUICK HARDENING MATERIAL AND QUICK HARDENING CEMENT COMPOSITION USING THE SAME
PROBLEM TO BE SOLVED: To provide a quick hardening material excellent in stability of dimension with less length change in both of in-air curing and in-water curing, and excellent in quick hardening property, and a quick hardening cement composition.SOLUTION: There are provided (1) a quick hardening material containing an amorphous calcium aluminate clinker ground article with Blaine specific surface area of 4000 to 8500 cm/g, alumina cement with Blaine specific surface area of 3000 to 6500 cm/g, and gypsum, in which Blaine specific surface area of the alumina cement is smaller than that of the amorphous calcium aluminate clinker ground article, (2) a quick hardening material having content molar ratio of CaO and AlOin the amorphous calcium aluminate clinker of 1.3 to 2.5, (3) a quick hardening material containing the alumina cement of 5 to 20 pts.mass based on 100 pts.mass of the amorphous calcium aluminate clinker ground article, and (4) a quick hardening cement composition containing cement and any of quick hardening material (1) to (3).SELECTED DRAWING: None
【課題】気中養生及び水中養生のいずれにおいても長さ変化が少なく寸法の安定性に優れ、急硬性にも優れた急硬材及びそれを用いた急硬性セメント組成物を提供する。【解決手段】（１）ブレーン比表面積が４０００〜８５００ｃｍ２／ｇである非晶質カルシウムアルミネートクリンカー粉砕物、ブレーン比表面積が３０００〜６５００ｃｍ２／ｇであるアルミナセメント、石膏を含有してなり、アルミナセメントのブレーン比表面積が非晶質カルシウムアルミネートクリンカー粉砕物のブレーン比表面積よりも小さい急硬材、（２）非晶質カルシウムアルミネートクリンカーのＣａＯとＡｌ2Ｏ3の含有モル比が１.３〜２．５である急硬材、（３）非晶質カルシウムアルミネートクリンカー粉砕物１００質量部に対してアルミナセメントが５〜２０質量部である急硬材、（４）セメントと（１）〜（３）のいずれかの急硬材を含有する急硬性セメント組成物。【選択図】 なし
QUICK HARDENING MATERIAL AND QUICK HARDENING CEMENT COMPOSITION USING THE SAME
PROBLEM TO BE SOLVED: To provide a quick hardening material excellent in stability of dimension with less length change in both of in-air curing and in-water curing, and excellent in quick hardening property, and a quick hardening cement composition.SOLUTION: There are provided (1) a quick hardening material containing an amorphous calcium aluminate clinker ground article with Blaine specific surface area of 4000 to 8500 cm/g, alumina cement with Blaine specific surface area of 3000 to 6500 cm/g, and gypsum, in which Blaine specific surface area of the alumina cement is smaller than that of the amorphous calcium aluminate clinker ground article, (2) a quick hardening material having content molar ratio of CaO and AlOin the amorphous calcium aluminate clinker of 1.3 to 2.5, (3) a quick hardening material containing the alumina cement of 5 to 20 pts.mass based on 100 pts.mass of the amorphous calcium aluminate clinker ground article, and (4) a quick hardening cement composition containing cement and any of quick hardening material (1) to (3).SELECTED DRAWING: None
【課題】気中養生及び水中養生のいずれにおいても長さ変化が少なく寸法の安定性に優れ、急硬性にも優れた急硬材及びそれを用いた急硬性セメント組成物を提供する。【解決手段】（１）ブレーン比表面積が４０００〜８５００ｃｍ２／ｇである非晶質カルシウムアルミネートクリンカー粉砕物、ブレーン比表面積が３０００〜６５００ｃｍ２／ｇであるアルミナセメント、石膏を含有してなり、アルミナセメントのブレーン比表面積が非晶質カルシウムアルミネートクリンカー粉砕物のブレーン比表面積よりも小さい急硬材、（２）非晶質カルシウムアルミネートクリンカーのＣａＯとＡｌ2Ｏ3の含有モル比が１.３〜２．５である急硬材、（３）非晶質カルシウムアルミネートクリンカー粉砕物１００質量部に対してアルミナセメントが５〜２０質量部である急硬材、（４）セメントと（１）〜（３）のいずれかの急硬材を含有する急硬性セメント組成物。【選択図】 なし
QUICK HARDENING MATERIAL AND QUICK HARDENING CEMENT COMPOSITION USING THE SAME
急硬材及びそれを用いた急硬性セメント組成物
USHIRO MASATAKA (author) / HIGUCHI TAKAYUKI (author)
2018-05-31
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
QUICK-HARDENING MATERIAL AND QUICK-HARDENING CEMENT COMPOSITION
| European Patent Office | 2019
| European Patent Office | 2016
QUICK-HARDENING CEMENT ADMIXTURE AND QUICK-HARDENING CEMENT COMPOSITION
| European Patent Office | 2017
QUICK-HARDENING ADMIXTURE AND QUICK-HARDENING CEMENT COMPOSITION
| European Patent Office | 2023
QUICK HARDENING AGENT FOR CEMENT, AND QUICK HARDENING CEMENT USING THE SAME
| European Patent Office | 2019