GROUND IMPROVEMENT MATERIAL SLURRY AND GROUND IMPROVEMENT METHOD
PROBLEM TO BE SOLVED: To provide a ground improvement material slurry and a ground improvement method, capable of achieving low carbon dioxide discharge amount, stable pressed sending of a slime and high strength development.SOLUTION: There is provided a ground improvement material slurry containing one or more kind selected from cement and blast furnace slag fine powder, one or more kind selected from a naphthalenesulfonate-based high performance water-reducing agent and polyacrylic acids, and a viscosity reducing agent consisting of alkali metal carbonate, and having high environment load reducing effect with total of carbon dioxide discharge amount of the used material of 200 kg or less per 1 m. There is provided a ground improvement method including spraying the ground improvement material slurry at spray pressure of 25 MPa or more and spray amount of 100 L/min. or more, in which viscosity of slime at 4 hours after mixing is 30,000 mPa s or less and disposal of the slime is easy.SELECTED DRAWING: None
【課題】二酸化炭素排出量が低く、スライムの安定的な圧送と高い強度発現が可能な地盤改良材料スラリーおよび地盤改良工法を提供する。【解決手段】セメントと高炉スラグ微粉末から選ばれる１種以上、並びに、ナフタレンスルホン酸塩系高性能減水剤とポリアクリル酸類から選ばれる１種以上およびアルカリ金属炭酸塩からなる粘性低減剤を含有してなる地盤改良材料スラリーであって、前記使用材料の二酸化炭素排出量の合計が１ｍ３あたり２００ｋｇ以下であることを特徴とする環境負荷低減効果の高い地盤改良材料スラリーである。さらに、前記地盤改良材料スラリーを用いて、噴射圧２５MPa以上、噴射量１００L/min以上で地盤に噴射することを特徴とする地盤改良工法であり、スライムの粘度が混合後４時間で３０,０００mPa・s以下であって、スライムの廃棄が容易であることを特徴とする地盤改良工法である。【選択図】なし
GROUND IMPROVEMENT MATERIAL SLURRY AND GROUND IMPROVEMENT METHOD
PROBLEM TO BE SOLVED: To provide a ground improvement material slurry and a ground improvement method, capable of achieving low carbon dioxide discharge amount, stable pressed sending of a slime and high strength development.SOLUTION: There is provided a ground improvement material slurry containing one or more kind selected from cement and blast furnace slag fine powder, one or more kind selected from a naphthalenesulfonate-based high performance water-reducing agent and polyacrylic acids, and a viscosity reducing agent consisting of alkali metal carbonate, and having high environment load reducing effect with total of carbon dioxide discharge amount of the used material of 200 kg or less per 1 m. There is provided a ground improvement method including spraying the ground improvement material slurry at spray pressure of 25 MPa or more and spray amount of 100 L/min. or more, in which viscosity of slime at 4 hours after mixing is 30,000 mPa s or less and disposal of the slime is easy.SELECTED DRAWING: None
【課題】二酸化炭素排出量が低く、スライムの安定的な圧送と高い強度発現が可能な地盤改良材料スラリーおよび地盤改良工法を提供する。【解決手段】セメントと高炉スラグ微粉末から選ばれる１種以上、並びに、ナフタレンスルホン酸塩系高性能減水剤とポリアクリル酸類から選ばれる１種以上およびアルカリ金属炭酸塩からなる粘性低減剤を含有してなる地盤改良材料スラリーであって、前記使用材料の二酸化炭素排出量の合計が１ｍ３あたり２００ｋｇ以下であることを特徴とする環境負荷低減効果の高い地盤改良材料スラリーである。さらに、前記地盤改良材料スラリーを用いて、噴射圧２５MPa以上、噴射量１００L/min以上で地盤に噴射することを特徴とする地盤改良工法であり、スライムの粘度が混合後４時間で３０,０００mPa・s以下であって、スライムの廃棄が容易であることを特徴とする地盤改良工法である。【選択図】なし
GROUND IMPROVEMENT MATERIAL SLURRY AND GROUND IMPROVEMENT METHOD
地盤改良材料スラリーおよび地盤改良工法
SASAKI TAKASHI (author) / WATANABE AKIRA (author) / KUSHIHASHI TAKUMI (author)
2018-08-09
Patent
Electronic Resource
Japanese
GROUND IMPROVEMENT MATERIAL SLURRY AND GROUND IMPROVEMENT CONSTRUCTION METHOD
| European Patent Office | 2022
| European Patent Office | 2022
| European Patent Office | 2022
GROUND IMPROVEMENT METHOD AND GROUND IMPROVEMENT MATERIAL
| European Patent Office | 2024