SOLID ELECTROLYTE SINTERED BODY, AND MANUFACTURING METHOD THEREFOR
To provide a solid electrolyte sintered body high in conductivity and having linear thermal expansion coefficient at same level as alumina, and a manufacturing method therefor.SOLUTION: A solid electrolyte sintered body contains cubic crystal ZrOin which ScOand AOare solid-solved, wherein A=one or more element selected from a group consisting of La, Ce, Sm, Nd, Yb and Y, and single monoclinic crystal ZrO, and has single monoclinic phase rate (X) of 10 to 40%. The solid electrolyte sintered body preferably has linear thermal expansion coefficient at 400°C to 1000°C of 8×10/°C to 9.5×10/°C, and conductivity at 600°C of 0.0060 S/cm or more. The solid electrolyte sintered body is obtained by mixing ScO, AOand single monoclinic ZrOto mold a mixture and burning a molded body at 1400°C to 1600°C for 2 to 5 h.SELECTED DRAWING: Figure 1
【課題】導電率が高く、かつ、アルミナと同程度の線熱膨張係数を持つ固体電解質焼結体、及びその製造方法を提供すること。【解決手段】固体電解質焼結体は、Ｓｃ2Ｏ3、及びＡ2Ｏ3（但し，Ａ＝Ｌａ、Ｃｅ、Ｓｍ、Ｎｄ、Ｙｂ、及びＹからなる群から選ばれるいずれか１以上の元素）が固溶した立方晶ＺｒＯ2と、単斜晶ＺｒＯ2とを含み、単斜晶相率（Ｘ）が１０〜４０％であるものからなる。固体電解質焼結体は、４００℃〜１０００℃の線熱膨張係数が８×１０-6／℃以上９．５×１０-6／℃以下であり、６００℃における導電率が０．００６０Ｓ／ｃｍ以上であるものが好ましい。このような固体電解質焼結体は、Ｓｃ2Ｏ3、Ａ2Ｏ3、及び単斜晶ＺｒＯ2を混合し、混合物を成形し、成形体を１４００℃以上１６００℃以下で２〜５ｈ焼成することにより得られる。【選択図】図１
SOLID ELECTROLYTE SINTERED BODY, AND MANUFACTURING METHOD THEREFOR
To provide a solid electrolyte sintered body high in conductivity and having linear thermal expansion coefficient at same level as alumina, and a manufacturing method therefor.SOLUTION: A solid electrolyte sintered body contains cubic crystal ZrOin which ScOand AOare solid-solved, wherein A=one or more element selected from a group consisting of La, Ce, Sm, Nd, Yb and Y, and single monoclinic crystal ZrO, and has single monoclinic phase rate (X) of 10 to 40%. The solid electrolyte sintered body preferably has linear thermal expansion coefficient at 400°C to 1000°C of 8×10/°C to 9.5×10/°C, and conductivity at 600°C of 0.0060 S/cm or more. The solid electrolyte sintered body is obtained by mixing ScO, AOand single monoclinic ZrOto mold a mixture and burning a molded body at 1400°C to 1600°C for 2 to 5 h.SELECTED DRAWING: Figure 1
【課題】導電率が高く、かつ、アルミナと同程度の線熱膨張係数を持つ固体電解質焼結体、及びその製造方法を提供すること。【解決手段】固体電解質焼結体は、Ｓｃ2Ｏ3、及びＡ2Ｏ3（但し，Ａ＝Ｌａ、Ｃｅ、Ｓｍ、Ｎｄ、Ｙｂ、及びＹからなる群から選ばれるいずれか１以上の元素）が固溶した立方晶ＺｒＯ2と、単斜晶ＺｒＯ2とを含み、単斜晶相率（Ｘ）が１０〜４０％であるものからなる。固体電解質焼結体は、４００℃〜１０００℃の線熱膨張係数が８×１０-6／℃以上９．５×１０-6／℃以下であり、６００℃における導電率が０．００６０Ｓ／ｃｍ以上であるものが好ましい。このような固体電解質焼結体は、Ｓｃ2Ｏ3、Ａ2Ｏ3、及び単斜晶ＺｒＯ2を混合し、混合物を成形し、成形体を１４００℃以上１６００℃以下で２〜５ｈ焼成することにより得られる。【選択図】図１
SOLID ELECTROLYTE SINTERED BODY, AND MANUFACTURING METHOD THEREFOR
固体電解質焼結体、及びその製造方法
NAKAMURA TADASHI (author) / SAITO TOMOMI (author) / NOMURA KAZUHIRO (author)
2018-12-06
Patent
Electronic Resource
Japanese
ZIRCONIA SINTERED BODY AND MANUFACTURING METHOD THEREFOR
| European Patent Office | 2020
ZIRCONIA SINTERED BODY AND MANUFACTURING METHOD THEREFOR
| European Patent Office | 2023
ZIRCONIA SINTERED BODY AND MANUFACTURING METHOD THEREFOR
| European Patent Office | 2015