ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
To provide an admixture capable of early providing sufficient demolding strength under a curing condition of a temperature generally applied in steam curing (for example about 50 to 70°C) even without applying specific cement, and sufficiently small in effect on change with time of flowability of a mortar composition and a concrete composition.SOLUTION: The admixture for mortar and concrete satisfies all conditions represented by inequality of the following (1) to (4), 10≤0.00083×A+0.24212×B+0.87668×C+1.4978×D+0.03276×A×B+5.65 (1). 3≤B<16 (2). 0
【課題】特殊なセメントを適用しなくても、蒸気養生において一般に適用される温度（例えば、５０〜７０℃程度）の養生条件で早期に十分な脱型強度を得られるとともに、モルタル組成物及びコンクリート組成物の流動性の経時的変化に及ぼす影響が十分に小さい、モルタル・コンクリート用混和材の提供。【解決手段】本発明に係るモルタル・コンクリート用混和材は、早強ポルトランドセメントの含有量をＡｋｇ／２０ｋｇ、半水石膏及び無水石膏の少なくとも一方の石膏の含有量をＢｋｇ／２０ｋｇ、珪酸ナトリウムの含有量をＣｋｇ／２０ｋｇ、硫酸アルミニウムの含有量をＤｋｇ／２０ｋｇとしたとき、以下の（１）〜（４）の不等式で表される全ての条件を満たす。10≦0.00083×Ａ＋0.24212×Ｂ＋0.87668×Ｃ＋1.4978×Ｄ＋0.03276×Ａ×Ｂ＋5.65…（１）、3≦Ｂ＜１６…（２）、０＜Ｃ＜２…（３）、０＜Ｄ＜２…（４）【選択図】図４
ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
To provide an admixture capable of early providing sufficient demolding strength under a curing condition of a temperature generally applied in steam curing (for example about 50 to 70°C) even without applying specific cement, and sufficiently small in effect on change with time of flowability of a mortar composition and a concrete composition.SOLUTION: The admixture for mortar and concrete satisfies all conditions represented by inequality of the following (1) to (4), 10≤0.00083×A+0.24212×B+0.87668×C+1.4978×D+0.03276×A×B+5.65 (1). 3≤B<16 (2). 0
【課題】特殊なセメントを適用しなくても、蒸気養生において一般に適用される温度（例えば、５０〜７０℃程度）の養生条件で早期に十分な脱型強度を得られるとともに、モルタル組成物及びコンクリート組成物の流動性の経時的変化に及ぼす影響が十分に小さい、モルタル・コンクリート用混和材の提供。【解決手段】本発明に係るモルタル・コンクリート用混和材は、早強ポルトランドセメントの含有量をＡｋｇ／２０ｋｇ、半水石膏及び無水石膏の少なくとも一方の石膏の含有量をＢｋｇ／２０ｋｇ、珪酸ナトリウムの含有量をＣｋｇ／２０ｋｇ、硫酸アルミニウムの含有量をＤｋｇ／２０ｋｇとしたとき、以下の（１）〜（４）の不等式で表される全ての条件を満たす。10≦0.00083×Ａ＋0.24212×Ｂ＋0.87668×Ｃ＋1.4978×Ｄ＋0.03276×Ａ×Ｂ＋5.65…（１）、3≦Ｂ＜１６…（２）、０＜Ｃ＜２…（３）、０＜Ｄ＜２…（４）【選択図】図４
ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
モルタル・コンクリート用混和材、これを含むセメント組成物、モルタル組成物及びコンクリート組成物、並びに、モルタル硬化物及びコンクリート硬化物の製造方法
YOSHIDA KOICHIRO (author) / SATO YOSHIHIDE (author) / KIRIYAMA HIROKAZU (author)
2020-01-09
Patent
Electronic Resource
Japanese