ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
To provide an admixture capable of early providing sufficient demolding strength under a curing condition of a temperature generally applied in steam curing (for example about 50 to 70°C) even without applying specific cement, and sufficiently small in effect on change with time of flowability of a mortar composition and a concrete composition.SOLUTION: The admixture for mortar and concrete according to the present invention includes high-early- strength Portland cement, at least one gypsum of hemihydrate gypsum and anhydrous gypsum, sodium silicate, aluminum sulfate, silica fume, wherein percentage content of the high-early-strength Portland cement is over 0 mass% and 45 mass% or less, percentage content of the gypsum is 30 mass% to 65 mass%, percentage content of the sodium silicate is over 0 mass% and less than 10 mass%, percentage content of the aluminum sulfate is over 0 mass% and less than 10 mass%, and percentage content of the silica fume is 20 mass% to 70 mass%, based on total mass of the admixture.SELECTED DRAWING: None
【課題】特殊なセメントを適用しなくても、蒸気養生において一般に適用される温度（例えば、５０〜７０℃程度）の養生条件で早期に十分な脱型強度を得ることができるとともに、モルタル組成物及びコンクリート組成物の流動性の経時的変化に及ぼす影響が十分に小さい混和材を提供する。【解決手段】本発明に係るモルタル・コンクリート用混和材は、早強ポルトランドセメントと、半水石膏及び無水石膏の少なくとも一方の石膏と、珪酸ナトリウムと、硫酸アルミニウムと、シリカフュームとを含み、当該混和材の全質量を基準として、早強ポルトランドセメントの含有率が０質量％超４５質量％以下であり、上記石膏の含有率が３０質量％以上６５質量％以下であり、珪酸ナトリウムの含有率が０質量％超１０質量％未満であり、硫酸アルミニウムの含有率が０質量％超１０質量％未満であり、シリカフュームの含有率が２０質量％以上７０質量％以下である。【選択図】なし
ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
To provide an admixture capable of early providing sufficient demolding strength under a curing condition of a temperature generally applied in steam curing (for example about 50 to 70°C) even without applying specific cement, and sufficiently small in effect on change with time of flowability of a mortar composition and a concrete composition.SOLUTION: The admixture for mortar and concrete according to the present invention includes high-early- strength Portland cement, at least one gypsum of hemihydrate gypsum and anhydrous gypsum, sodium silicate, aluminum sulfate, silica fume, wherein percentage content of the high-early-strength Portland cement is over 0 mass% and 45 mass% or less, percentage content of the gypsum is 30 mass% to 65 mass%, percentage content of the sodium silicate is over 0 mass% and less than 10 mass%, percentage content of the aluminum sulfate is over 0 mass% and less than 10 mass%, and percentage content of the silica fume is 20 mass% to 70 mass%, based on total mass of the admixture.SELECTED DRAWING: None
【課題】特殊なセメントを適用しなくても、蒸気養生において一般に適用される温度（例えば、５０〜７０℃程度）の養生条件で早期に十分な脱型強度を得ることができるとともに、モルタル組成物及びコンクリート組成物の流動性の経時的変化に及ぼす影響が十分に小さい混和材を提供する。【解決手段】本発明に係るモルタル・コンクリート用混和材は、早強ポルトランドセメントと、半水石膏及び無水石膏の少なくとも一方の石膏と、珪酸ナトリウムと、硫酸アルミニウムと、シリカフュームとを含み、当該混和材の全質量を基準として、早強ポルトランドセメントの含有率が０質量％超４５質量％以下であり、上記石膏の含有率が３０質量％以上６５質量％以下であり、珪酸ナトリウムの含有率が０質量％超１０質量％未満であり、硫酸アルミニウムの含有率が０質量％超１０質量％未満であり、シリカフュームの含有率が２０質量％以上７０質量％以下である。【選択図】なし
ADMIXTURE FOR MORTAR AND CONCRETE, CEMENT COMPOSITION, MORTAR COMPOSITION AND CONCRETE COMPOSITION EACH INCLUDING THE ADMIXTURE, AND MANUFACTURING METHODS OF MORTAR CURED ARTICLE AND CONCRETE CURED ARTICLE
モルタル・コンクリート用混和材、これを含むセメント組成物、モルタル組成物及びコンクリート組成物、並びに、モルタル硬化物及びコンクリート硬化物の製造方法
YOSHIDA KOICHIRO (author) / SATO YOSHIHIDE (author) / KIRIYAMA HIROKAZU (author)
2020-01-09
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME