SPRAY CONCRETE
To provide a spray concrete excellent in fast curing capability and further excellent in initial and long-term strength-developing properties.SOLUTION: A spray concrete comprises 7-14 pts.mass of an accelerator (B) based on 100 pts.mass of a cement in a base concrete (A). The base concrete (A) comprises: 100 pts.mass of the cement; 7-16 pts.mass (in terms of an anhydride) of calcium sulfate having a Blaine specific surface area of 3,500-16,000 cm2/g; an aggregate; and water. The accelerator (B) comprises, based on a total mass of the accelerator (B): 68-87 mass% of calcium aluminate having a content molar ratio (CaO/Al2O3) of CaO and Al2O3 as chemical components of 1.8-2.7; 5-17 mass% (in terms of the anhydride) of alkali earth metal sulfate; an alkali metal sulfate; and an alkali metal carbonate, wherein a mass ratio (( the mass of alkali metal sulfate)/(the mass of alkali metal carbonate) of the alkali metal sulfate and the alkali metal carbonate (in terms of the anhydride) is 1.2-8.5.SELECTED DRAWING: None
【課題】急結性に優れ、且つ、初期及び長期の強度発現性にも優れる吹付コンクリートを提供する。【解決手段】急結材（Ｂ）の含有量がベースコンクリート（Ａ）中のセメント１００質量部に対して７〜１４質量部である吹付コンクリート。（Ａ）：セメント１００質量部、ブレーン比表面積３５００〜１６０００ｃｍ２／ｇの硫酸カルシウム７〜１６質量部（無水物換算）、骨材及び水を含むベースコンクリート。（Ｂ）：急結材（Ｂ）全質量を基準として、化学成分としてのＣａＯとＡｌ２Ｏ３の含有モル比（ＣａＯ／Ａｌ２Ｏ３）が１．８〜２．７のカルシウムアルミネートを６８〜８７質量％、アルカリ土類金属硫酸塩を無水物換算で５〜１７質量％、アルカリ金属硫酸塩及びアルカリ金属炭酸塩を含み、アルカリ金属硫酸塩及びアルカリ金属炭酸塩が質量比（アルカリ金属硫酸塩の質量／アルカリ金属炭酸塩の質量、無水物換算）で１．２〜８．５である急結材。【選択図】なし
SPRAY CONCRETE
To provide a spray concrete excellent in fast curing capability and further excellent in initial and long-term strength-developing properties.SOLUTION: A spray concrete comprises 7-14 pts.mass of an accelerator (B) based on 100 pts.mass of a cement in a base concrete (A). The base concrete (A) comprises: 100 pts.mass of the cement; 7-16 pts.mass (in terms of an anhydride) of calcium sulfate having a Blaine specific surface area of 3,500-16,000 cm2/g; an aggregate; and water. The accelerator (B) comprises, based on a total mass of the accelerator (B): 68-87 mass% of calcium aluminate having a content molar ratio (CaO/Al2O3) of CaO and Al2O3 as chemical components of 1.8-2.7; 5-17 mass% (in terms of the anhydride) of alkali earth metal sulfate; an alkali metal sulfate; and an alkali metal carbonate, wherein a mass ratio (( the mass of alkali metal sulfate)/(the mass of alkali metal carbonate) of the alkali metal sulfate and the alkali metal carbonate (in terms of the anhydride) is 1.2-8.5.SELECTED DRAWING: None
【課題】急結性に優れ、且つ、初期及び長期の強度発現性にも優れる吹付コンクリートを提供する。【解決手段】急結材（Ｂ）の含有量がベースコンクリート（Ａ）中のセメント１００質量部に対して７〜１４質量部である吹付コンクリート。（Ａ）：セメント１００質量部、ブレーン比表面積３５００〜１６０００ｃｍ２／ｇの硫酸カルシウム７〜１６質量部（無水物換算）、骨材及び水を含むベースコンクリート。（Ｂ）：急結材（Ｂ）全質量を基準として、化学成分としてのＣａＯとＡｌ２Ｏ３の含有モル比（ＣａＯ／Ａｌ２Ｏ３）が１．８〜２．７のカルシウムアルミネートを６８〜８７質量％、アルカリ土類金属硫酸塩を無水物換算で５〜１７質量％、アルカリ金属硫酸塩及びアルカリ金属炭酸塩を含み、アルカリ金属硫酸塩及びアルカリ金属炭酸塩が質量比（アルカリ金属硫酸塩の質量／アルカリ金属炭酸塩の質量、無水物換算）で１．２〜８．５である急結材。【選択図】なし