To reduce a linear change rate to prevent a crack from occurring in a castable refractory for a lance while improving the corrosion resistance thereof.SOLUTION: There is provided an alumina-magnesia based castable refractory for a lance. The refractory aggregate includes 5 mass% or more and 35 mass% or less of an alumina raw material, 0.5 mass% or more and 5 mass% or less of a magnesia raw material, and 55 mass% or more and 85 mass% or less of a spinel raw material. A carbon raw material is added to the refractory aggregate in an amount of 1 mass% or more and 10 mass% or less. Silicon nitride iron is added in an amount of 0.5 mass% or more and 10 mass% or less in outer percentage and metallic aluminum is added in an amount of less than 1 mass% in outer percentage, relative to the total of 100 mass% of the raw materials. The expansion of the refractory is suppressed by the shrinkage resulting from the progress of sintering, by adding the silicon nitride iron.SELECTED DRAWING: None
【課題】ランス用キャスタブル耐火物の耐食性を向上しつつ、線変化率を低減し亀裂を抑制する。【解決手段】アルミナ－マグネシア質のランス用キャスタブル耐火物である。耐火物骨材としては、アルミナ原料が５質量％以上３５質量％以下、マグネシア原料が０．５質量％以上５質量％以下で、更にスピネル原料が５５質量％以上８５質量％以下である。この耐火物骨材に炭素原料が１質量％以上１０質量％以下添加される。上記原料の合計１００質量％に対し、窒化珪素鉄を外掛け０.５質量％以上１０質量％以下、金属アルミニウムを外掛け１質量％未満、添加する。上記窒化珪素鉄の添加により、焼結が進行して収縮することにより膨張が抑制される。【選択図】なし
To reduce a linear change rate to prevent a crack from occurring in a castable refractory for a lance while improving the corrosion resistance thereof.SOLUTION: There is provided an alumina-magnesia based castable refractory for a lance. The refractory aggregate includes 5 mass% or more and 35 mass% or less of an alumina raw material, 0.5 mass% or more and 5 mass% or less of a magnesia raw material, and 55 mass% or more and 85 mass% or less of a spinel raw material. A carbon raw material is added to the refractory aggregate in an amount of 1 mass% or more and 10 mass% or less. Silicon nitride iron is added in an amount of 0.5 mass% or more and 10 mass% or less in outer percentage and metallic aluminum is added in an amount of less than 1 mass% in outer percentage, relative to the total of 100 mass% of the raw materials. The expansion of the refractory is suppressed by the shrinkage resulting from the progress of sintering, by adding the silicon nitride iron.SELECTED DRAWING: None
【課題】ランス用キャスタブル耐火物の耐食性を向上しつつ、線変化率を低減し亀裂を抑制する。【解決手段】アルミナ－マグネシア質のランス用キャスタブル耐火物である。耐火物骨材としては、アルミナ原料が５質量％以上３５質量％以下、マグネシア原料が０．５質量％以上５質量％以下で、更にスピネル原料が５５質量％以上８５質量％以下である。この耐火物骨材に炭素原料が１質量％以上１０質量％以下添加される。上記原料の合計１００質量％に対し、窒化珪素鉄を外掛け０.５質量％以上１０質量％以下、金属アルミニウムを外掛け１質量％未満、添加する。上記窒化珪素鉄の添加により、焼結が進行して収縮することにより膨張が抑制される。【選択図】なし
CASTABLE REFRACTORY FOR LANCE
ランス用キャスタブル耐火物
IKOMA YASUAKI (author)
2024-08-13
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
B22D
CASTING OF METALS
,
Gießen von Metallen
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
CASTABLE REFRACTORY COMPOSITION, CASTABLE REFRACTORY, AND METHOD OF PRODUCING CASTABLE REFRACTORY