PRECAST CONCRETE STRUCTURE AND MANUFACTURING METHOD THEREOF
A fiber-reinforced precast concrete structure of the present invention comprises: a precast concrete composition (10) including 30 to 80 wt% of cement, 1 to 10 wt% of an expansion material, 5 to 53 wt% of silica sand, 0.1 to 1 wt% of a polymer, 0.1 to 2 wt% of a fluidizing agent, 0.1 to 1 wt% of a fiber reinforcement material, 13 to 30 wt% of water, and 1 to 50 wt% of a binder; and reinforcing fibers (20) embedded in the concrete composition (10) or bonded to the upper and lower surfaces, respectively. The precast concrete structure is generally manufactured by embedding reinforcing bars inside the concrete. The concrete has excellent compressive strength but has a low tensile strength (1/11 level of compression resistance). Therefore, to compensate for this, the reinforcing bars were embedded in the concrete to resist the tensile force. When the reinforcing bars are embedded in the concrete, it is necessary to secure the thickness of the cover in order to secure the corrosion and bonding strength of the reinforcing bars. Therefore, the size of the precast concrete structure increases and its own weight becomes heavy. The present invention is a technology for reducing the thickness of a precast concrete structure and reducing its own weight by embedding the reinforcing fibers that replace the reinforcing bars in the concrete.
본 발명의 섬유보강 프리캐스트 콘크리트 구조물은 시멘트 30~80 중량%, 팽창재 1~10 중량%, 규사 5~53 중량%, 폴리머 0.1~1 중량%, 유동화제 0.1~2 중량%, 섬유보강재 0.1~1 중량%, 물 13~30 중량%, 바인더 1~ 50 중량%,를 포함하는 캐프리스트 콘크리트 조성물(10); 콘크리트 조성물(10)에 매립되거나 상면과 하면에 각각 결합되는 보강섬유(20);를 포함한다.프리캐스트 콘크리트 구조물은 일반적으로 콘크리트 내부에 철근을 매립하여 제작한다. 콘크리트는 압축강도가 우수하지만 인장강도(압축저항성의 1/11 수준)가 낮은 단점이 있다. 때문에 이를 보완하기 위해 콘크리트 내부에 철근을 매립하여 인장력에 저항하도록 한 것이다. 철근이 콘크리트에 매립되면 철근의 부식과 접합강도를 확보하기 위해, 피복두께를 확보해야 한다. 따라서 프리캐스트 콘크리트 구조물의 크기가 커지고 자중이 무거워지게 된다.본 발명은 콘크리트 내부에 철근을 대체한 보강섬유를 매립하여 프리캐스트 콘크리트 구조물의 두께를 줄이고, 자중을 감소시키는 기술이다.
PRECAST CONCRETE STRUCTURE AND MANUFACTURING METHOD THEREOF
A fiber-reinforced precast concrete structure of the present invention comprises: a precast concrete composition (10) including 30 to 80 wt% of cement, 1 to 10 wt% of an expansion material, 5 to 53 wt% of silica sand, 0.1 to 1 wt% of a polymer, 0.1 to 2 wt% of a fluidizing agent, 0.1 to 1 wt% of a fiber reinforcement material, 13 to 30 wt% of water, and 1 to 50 wt% of a binder; and reinforcing fibers (20) embedded in the concrete composition (10) or bonded to the upper and lower surfaces, respectively. The precast concrete structure is generally manufactured by embedding reinforcing bars inside the concrete. The concrete has excellent compressive strength but has a low tensile strength (1/11 level of compression resistance). Therefore, to compensate for this, the reinforcing bars were embedded in the concrete to resist the tensile force. When the reinforcing bars are embedded in the concrete, it is necessary to secure the thickness of the cover in order to secure the corrosion and bonding strength of the reinforcing bars. Therefore, the size of the precast concrete structure increases and its own weight becomes heavy. The present invention is a technology for reducing the thickness of a precast concrete structure and reducing its own weight by embedding the reinforcing fibers that replace the reinforcing bars in the concrete.
본 발명의 섬유보강 프리캐스트 콘크리트 구조물은 시멘트 30~80 중량%, 팽창재 1~10 중량%, 규사 5~53 중량%, 폴리머 0.1~1 중량%, 유동화제 0.1~2 중량%, 섬유보강재 0.1~1 중량%, 물 13~30 중량%, 바인더 1~ 50 중량%,를 포함하는 캐프리스트 콘크리트 조성물(10); 콘크리트 조성물(10)에 매립되거나 상면과 하면에 각각 결합되는 보강섬유(20);를 포함한다.프리캐스트 콘크리트 구조물은 일반적으로 콘크리트 내부에 철근을 매립하여 제작한다. 콘크리트는 압축강도가 우수하지만 인장강도(압축저항성의 1/11 수준)가 낮은 단점이 있다. 때문에 이를 보완하기 위해 콘크리트 내부에 철근을 매립하여 인장력에 저항하도록 한 것이다. 철근이 콘크리트에 매립되면 철근의 부식과 접합강도를 확보하기 위해, 피복두께를 확보해야 한다. 따라서 프리캐스트 콘크리트 구조물의 크기가 커지고 자중이 무거워지게 된다.본 발명은 콘크리트 내부에 철근을 대체한 보강섬유를 매립하여 프리캐스트 콘크리트 구조물의 두께를 줄이고, 자중을 감소시키는 기술이다.
PRECAST CONCRETE STRUCTURE AND MANUFACTURING METHOD THEREOF
섬유보강 프리캐스트 콘크리트 구조물 및 그 제작방법
LEE CHIN YONG (author) / JO MIN SU (author)
2020-12-10
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
E04B
Allgemeine Baukonstruktionen
,
GENERAL BUILDING CONSTRUCTIONS
PRECAST CONCRETE FOUNDATION AND MANUFACTURING METHOD THEREOF
| European Patent Office | 2018
PRECAST CONCRETE MEMBER AND MANUFACTURING METHOD OF PRECAST CONCRETE MEMBER
| European Patent Office | 2024
| European Patent Office | 2018