Method of manufacturing binder pitch from petroleum by-product
The present invention provides a method for manufacturing a binder pitch from a petrochemical by-product, which comprises the following steps: manufacturing a solid component by first heat treatment at the temperature of 340 to 420C (step 1); extracting a gasoline fraction by subjecting the solid component manufactured in the step 1 to secondary heat treatment at the temperature of 700 to 900C (step 2); and subjecting the petroleum fraction extracted in the step 2 to tertiary heat treatment at the temperature of 150 to 250C to manufacture a binder pitch (step 3). The method for manufacturing a binder pitch according to the present invention can manufacture a binder pitch having a softening point of 100 to 150C from petroleum-based low-grade raw materials and omit a secondary softening point adjusting step for controlling the softening point.
본 발명은 석유화학 부산물을 340 ℃ 내지 420 ℃의 온도에서 1 차 열처리하여 고형분을 제조하는 단계(단계 1); 상기 단계 1에서 제조된 고형분을 700 ℃ 내지 900 ℃의 온도에서 2 차 열처리하여 휘발유분을 추출하는 단계(단계 2); 및 상기 단계 2에서 추출된 휘발유분을 150 ℃ 내지 250 ℃의 온도에서 3 차 열처리하여 바인더 피치를 제조하는 단계(단계 3);를 포함하는 바인더 피치의 제조방법을 제공한다. 본 발명에 따른 바인더 피치의 제조방법은 석유계 저급원료로부터 100 ℃ 내지 150 ℃의 연화점을 갖는 바인더 피치를 제조할 수 있으며, 연화점 제어를 위한 2 차적인 연화점 조절 단계를 생략할 수 있다.
Method of manufacturing binder pitch from petroleum by-product
The present invention provides a method for manufacturing a binder pitch from a petrochemical by-product, which comprises the following steps: manufacturing a solid component by first heat treatment at the temperature of 340 to 420C (step 1); extracting a gasoline fraction by subjecting the solid component manufactured in the step 1 to secondary heat treatment at the temperature of 700 to 900C (step 2); and subjecting the petroleum fraction extracted in the step 2 to tertiary heat treatment at the temperature of 150 to 250C to manufacture a binder pitch (step 3). The method for manufacturing a binder pitch according to the present invention can manufacture a binder pitch having a softening point of 100 to 150C from petroleum-based low-grade raw materials and omit a secondary softening point adjusting step for controlling the softening point.
본 발명은 석유화학 부산물을 340 ℃ 내지 420 ℃의 온도에서 1 차 열처리하여 고형분을 제조하는 단계(단계 1); 상기 단계 1에서 제조된 고형분을 700 ℃ 내지 900 ℃의 온도에서 2 차 열처리하여 휘발유분을 추출하는 단계(단계 2); 및 상기 단계 2에서 추출된 휘발유분을 150 ℃ 내지 250 ℃의 온도에서 3 차 열처리하여 바인더 피치를 제조하는 단계(단계 3);를 포함하는 바인더 피치의 제조방법을 제공한다. 본 발명에 따른 바인더 피치의 제조방법은 석유계 저급원료로부터 100 ℃ 내지 150 ℃의 연화점을 갖는 바인더 피치를 제조할 수 있으며, 연화점 제어를 위한 2 차적인 연화점 조절 단계를 생략할 수 있다.
Method of manufacturing binder pitch from petroleum by-product
석유화학 부산물로부터 바인더 피치의 제조방법
LEE CHUL WEE (author) / IM JI SUN (author) / KIM JONG GU (author) / KIM JI HONG (author)
2017-11-29
Patent
Electronic Resource
Korean
Method of manufacturing binder pitch from petroleum by-product
European Patent Office | 2017
| European Patent Office | 2023
European Patent Office | 2023
IMPROVED BINDER PITCH FOR USE IN CARBON COMPOSITE MATERIALS
| European Patent Office | 2023