The present invention relates to a technology for improving non-flammable performance in constructing a high-density vacuum extrusion cement binder and, more specifically, corresponds to a technology to control residual flames caused by gases during combustion of existing polypropylene fibers and pulp fibers. According to the present invention, the composition is formed by replacing alkali-resistant glass fiber with a combustion temperature of 941 degrees Celsius and uses a predetermined amount of fly ash having voids formed therein, instead of a cement binder, to prevent detonation due to internal expansion when the temperature is increased. Accordingly, the high-density cement extrusion panel composition with increased heat resistance controls gas ejection due to combustion of fibers when heated, increases heat resistance of the material to control flame due to heating, and controls the expansion pressure of the composition by utilizing the internal voids, thereby providing an anti-explosion effect. The composition comprises: 30 to 60 wt% of Portland cement; 1 to 13 wt% of Fly ash; 38.0 to 58.5 wt% of filler; 1.5 to 5.5 wt% of reinforcing fiber; and 0.27 to 0.50 wt% of thickener.
본 발명은 고밀도 진공 압출성형 시멘트 결합물을 구성하는데 있어서 불연성능을 개선하기 위한 기술로서, 기존 폴리프로필렌 섬유와 펄프 섬유의 연소 중 가스에 의한 잔염을 제어하기 위한 기술에 해당한다. 본 발명에서는 연소온도가 섭씨 941도인 내알칼리성 유리섬유를 대체하여 조성물을 구성하였으며, 온도 가열시 내부 팽창에 의한 폭열 방지를 위하여 소재 내 공극을 가지고 있는 플라이애시를 시멘트 결합재 대신 일정량 사용하였다. 이러한 본 발명에 따른 "내열성이 향상된 고밀도 시멘트 압출성형 패널 조성물"은 온도가열시 섬유의 연소에 의한 가스 분출을 제어하고, 소재 자체 내의 내열성을 향상하여 가열에 따른 불꽃을 제어할 수 있을 뿐만 아니라 조성물을 내부 공극을 활용하여 팽창압을 제어함으로써 폭열 방지 효과도 획득이 가능하다.
High-density cement extruded panel composition with improved heat resistance
The present invention relates to a technology for improving non-flammable performance in constructing a high-density vacuum extrusion cement binder and, more specifically, corresponds to a technology to control residual flames caused by gases during combustion of existing polypropylene fibers and pulp fibers. According to the present invention, the composition is formed by replacing alkali-resistant glass fiber with a combustion temperature of 941 degrees Celsius and uses a predetermined amount of fly ash having voids formed therein, instead of a cement binder, to prevent detonation due to internal expansion when the temperature is increased. Accordingly, the high-density cement extrusion panel composition with increased heat resistance controls gas ejection due to combustion of fibers when heated, increases heat resistance of the material to control flame due to heating, and controls the expansion pressure of the composition by utilizing the internal voids, thereby providing an anti-explosion effect. The composition comprises: 30 to 60 wt% of Portland cement; 1 to 13 wt% of Fly ash; 38.0 to 58.5 wt% of filler; 1.5 to 5.5 wt% of reinforcing fiber; and 0.27 to 0.50 wt% of thickener.
본 발명은 고밀도 진공 압출성형 시멘트 결합물을 구성하는데 있어서 불연성능을 개선하기 위한 기술로서, 기존 폴리프로필렌 섬유와 펄프 섬유의 연소 중 가스에 의한 잔염을 제어하기 위한 기술에 해당한다. 본 발명에서는 연소온도가 섭씨 941도인 내알칼리성 유리섬유를 대체하여 조성물을 구성하였으며, 온도 가열시 내부 팽창에 의한 폭열 방지를 위하여 소재 내 공극을 가지고 있는 플라이애시를 시멘트 결합재 대신 일정량 사용하였다. 이러한 본 발명에 따른 "내열성이 향상된 고밀도 시멘트 압출성형 패널 조성물"은 온도가열시 섬유의 연소에 의한 가스 분출을 제어하고, 소재 자체 내의 내열성을 향상하여 가열에 따른 불꽃을 제어할 수 있을 뿐만 아니라 조성물을 내부 공극을 활용하여 팽창압을 제어함으로써 폭열 방지 효과도 획득이 가능하다.
High-density cement extruded panel composition with improved heat resistance
내열성이 향상된 고밀도 시멘트 압출성형 패널 조성물 및 이를 이용하여 제조되는 고밀도 시멘트 압출성형 패널
SONG TAE HYEOB (author) / JANG KYONG PIL (author) / CHAE CHANG U (author) / KIM HEUNG YOUL (author)
2023-05-25
Patent
Electronic Resource
Korean
Extruded cement composite panel for formwork
| British Library Conference Proceedings | 2002
| European Patent Office | 2020
| European Patent Office | 2020