MORTAR COMPOSITION, MORTAR, AND MORTAR MANUFACTURING METHOD
The present invention provides a joint-part mortar for increasing the sealing property of a joint-part of a nozzle structure for ejecting molten steel. The joint-part motor is obtained by: adding, to 100% by mass of a mortar composition comprising not less than 10% by mass and not more than 20% by mass of unexpanded vermiculite, not less than 1% by mass and not more than 5% by mass of frit powder, and the remainder comprising other refractory raw material, not less than 22% by mass and not more than 45% by mass of an ethylene vinyl acetate emulsion with respect to the 100%, and not less than 1% by mass and not more than 5% by mass of plasticizer with respect to the 100%; kneading the mixture; pressure-molding the kneaded product; and drying a molded base material at not less than 60°C and not more than 100°C.
La présente invention concerne un mortier de jointement pour augmenter la propriété d'étanchéité d'un jointement d'une structure de buse pour éjecter de l'acier fondu. Le mortier de partie joint est obtenu par : ajout, à 100 % en masse d'une composition de mortier comprenant pas moins de 10 % en masse et pas plus de 20 % en masse de vermiculite non expansée, pas moins de 1 % en masse et pas plus de 5 % en masse de poudre de frittage, et le reste comprenant une autre matière première réfractaire, de pas moins de 22 % en masse et pas plus de 45 % en masse d'une émulsion d'éthylène-acétate de vinyle par rapport à 100 %, et de pas moins de 1 % en masse et pas plus de 5 % en masse de plastifiant par rapport à 100 % ; malaxage du mélange ; moulage sous pression du produit malaxé ; et séchage d'un matériau de base moulé à pas moins de 60 °C et pas plus de 100° C.
本発明は,溶鋼排出用のノズル構造体の目地部のシール性を高めるために,未膨張のバーミキュライトを10質量%以上20質量%以下,フリット粉を1質量%以上5質量%以下含み,残部がその他耐火原料からなるモルタル用配合物100質量%に,エチレン酢ビ系エマルジョンを外掛けで22質量%以上45質量%以下,可塑剤を外掛けで1質量%以上5質量%以下加えて混練し,当該混練物を加圧成形し成形した素地を60℃以上100℃以下で乾燥して得られる目地部用モルタルを提供する。
MORTAR COMPOSITION, MORTAR, AND MORTAR MANUFACTURING METHOD
The present invention provides a joint-part mortar for increasing the sealing property of a joint-part of a nozzle structure for ejecting molten steel. The joint-part motor is obtained by: adding, to 100% by mass of a mortar composition comprising not less than 10% by mass and not more than 20% by mass of unexpanded vermiculite, not less than 1% by mass and not more than 5% by mass of frit powder, and the remainder comprising other refractory raw material, not less than 22% by mass and not more than 45% by mass of an ethylene vinyl acetate emulsion with respect to the 100%, and not less than 1% by mass and not more than 5% by mass of plasticizer with respect to the 100%; kneading the mixture; pressure-molding the kneaded product; and drying a molded base material at not less than 60°C and not more than 100°C.
La présente invention concerne un mortier de jointement pour augmenter la propriété d'étanchéité d'un jointement d'une structure de buse pour éjecter de l'acier fondu. Le mortier de partie joint est obtenu par : ajout, à 100 % en masse d'une composition de mortier comprenant pas moins de 10 % en masse et pas plus de 20 % en masse de vermiculite non expansée, pas moins de 1 % en masse et pas plus de 5 % en masse de poudre de frittage, et le reste comprenant une autre matière première réfractaire, de pas moins de 22 % en masse et pas plus de 45 % en masse d'une émulsion d'éthylène-acétate de vinyle par rapport à 100 %, et de pas moins de 1 % en masse et pas plus de 5 % en masse de plastifiant par rapport à 100 % ; malaxage du mélange ; moulage sous pression du produit malaxé ; et séchage d'un matériau de base moulé à pas moins de 60 °C et pas plus de 100° C.
本発明は,溶鋼排出用のノズル構造体の目地部のシール性を高めるために,未膨張のバーミキュライトを10質量%以上20質量%以下,フリット粉を1質量%以上5質量%以下含み,残部がその他耐火原料からなるモルタル用配合物100質量%に,エチレン酢ビ系エマルジョンを外掛けで22質量%以上45質量%以下,可塑剤を外掛けで1質量%以上5質量%以下加えて混練し,当該混練物を加圧成形し成形した素地を60℃以上100℃以下で乾燥して得られる目地部用モルタルを提供する。
MORTAR COMPOSITION, MORTAR, AND MORTAR MANUFACTURING METHOD
COMPOSITION DE MORTIER, MORTIER ET PROCÉDÉ DE FABRICATION DE MORTIER
モルタル用配合物,モルタル及びモルタルの製造方法
OOUCHI TATSUYA (author) / FUKUNAGA SHINICHI (author)
2018-08-30
Patent
Electronic Resource
Japanese