ZIRCONIA SINTERED COMPACT HAVING HIGH LINEAR LIGHT TRANSMITTANCE
The present invention provides: a zirconia sintered compact that exhibits both excellent strength and translucency, as well as excellent linear light transmittance, without using a HIP apparatus; and a zirconia molded body and a zirconia provisionally sintered body with which such a zirconia sintered compact can be achieved. The present invention relates to a zirconia molded body comprising zirconia particles, which contain 2.0-9.0 mol% of yttria and have an average primary particle size of 60 nm or less and in which the amount of particles having a size greater than 100 nm is 0.5 mass% or less, wherein the ΔL*(W-B) value of the molded body is 5 or more at a thickness of 1.5 mm. The present invention also relates to a zirconia provisionally sintered body containing 2.0-9.0 mol% of yttria, and having a ΔL*(W-B) value of 5 or more at a thickness of 1.5 mm. The present invention further relates to a zirconia sintered compact containing a fluorescent agent and 2.0-9.0 mol% of yttria, and having a linear light transmittance of 1% or more at a thickness of 1.0 mm.
L'invention fournit un corps fritté en zircone qui ne met pas en œuvre de dispositif de compression isostatique à chaud, qui est à la fois excellent en termes de résistance et de translucidité, et qui présente une excellente transmittance de lumière linéaire. L'invention fournit également un corps moulé en zircone permettant de procurer un tel corps fritté en zircone, et un corps calciné en zircone. Le corps moulé en zircone de l'invention contient ２,０ à ９,０% en moles d'une yttria, est constitué de particules de zircone de diamètre particulaire primaire moyen inférieur ou égal à 60nm, et de 0,5% en masse ou moins de particules présentant un diamètre de grain dépassant 100nm, et est tel que ΔＬ＊（Ｗ－Ｂ） dans 1,5mm d'épaisseur est supérieur ou égal à 5. En outre, le corps calciné en zircone de l'invention contient ２,０ à ９,０% en moles d'une yttria, et est tel que ΔＬ＊（Ｗ－Ｂ） dans 1,5mm d'épaisseur est supérieur ou égal à 5. Enfin, le corps fritté en zircone de l'invention contient un agent fluorescent, et ２,０ à ９,０% en moles d'une yttria, et présente une transmittance de lumière linéaire dans 1,0mm d'épaisseur supérieure ou égale à 1%.
本発明は、ＨＩＰ装置を使用することなく、強度と透光性が共に優れ、かつ直線光透過率が優れたジルコニア焼結体、このようなジルコニア焼結体を与えることのできるジルコニア成形体およびジルコニア仮焼体を提供する。本発明は、イットリアを２．０～９．０ｍｏｌ％含み、平均一次粒子径が６０ｎｍ以下で、かつ１００ｎｍを超える粒径を有する粒子が０．５質量％以下であるジルコニア粒子からなり、厚さ１．５ｍｍにおけるΔＬ＊（Ｗ－Ｂ）が５以上である、ジルコニア成形体。また、イットリアを２．０～９．０ｍｏｌ％含み、厚さ１．５ｍｍにおけるΔＬ＊（Ｗ－Ｂ）が５以上である、ジルコニア仮焼体。さらに、蛍光剤と、２．０～９．０ｍｏｌ％のイットリアを含み、厚さ１．０ｍｍにおける直線光透過率が１％以上である、ジルコニア焼結体に関する。
ZIRCONIA SINTERED COMPACT HAVING HIGH LINEAR LIGHT TRANSMITTANCE
The present invention provides: a zirconia sintered compact that exhibits both excellent strength and translucency, as well as excellent linear light transmittance, without using a HIP apparatus; and a zirconia molded body and a zirconia provisionally sintered body with which such a zirconia sintered compact can be achieved. The present invention relates to a zirconia molded body comprising zirconia particles, which contain 2.0-9.0 mol% of yttria and have an average primary particle size of 60 nm or less and in which the amount of particles having a size greater than 100 nm is 0.5 mass% or less, wherein the ΔL*(W-B) value of the molded body is 5 or more at a thickness of 1.5 mm. The present invention also relates to a zirconia provisionally sintered body containing 2.0-9.0 mol% of yttria, and having a ΔL*(W-B) value of 5 or more at a thickness of 1.5 mm. The present invention further relates to a zirconia sintered compact containing a fluorescent agent and 2.0-9.0 mol% of yttria, and having a linear light transmittance of 1% or more at a thickness of 1.0 mm.
L'invention fournit un corps fritté en zircone qui ne met pas en œuvre de dispositif de compression isostatique à chaud, qui est à la fois excellent en termes de résistance et de translucidité, et qui présente une excellente transmittance de lumière linéaire. L'invention fournit également un corps moulé en zircone permettant de procurer un tel corps fritté en zircone, et un corps calciné en zircone. Le corps moulé en zircone de l'invention contient ２,０ à ９,０% en moles d'une yttria, est constitué de particules de zircone de diamètre particulaire primaire moyen inférieur ou égal à 60nm, et de 0,5% en masse ou moins de particules présentant un diamètre de grain dépassant 100nm, et est tel que ΔＬ＊（Ｗ－Ｂ） dans 1,5mm d'épaisseur est supérieur ou égal à 5. En outre, le corps calciné en zircone de l'invention contient ２,０ à ９,０% en moles d'une yttria, et est tel que ΔＬ＊（Ｗ－Ｂ） dans 1,5mm d'épaisseur est supérieur ou égal à 5. Enfin, le corps fritté en zircone de l'invention contient un agent fluorescent, et ２,０ à ９,０% en moles d'une yttria, et présente une transmittance de lumière linéaire dans 1,0mm d'épaisseur supérieure ou égale à 1%.
本発明は、ＨＩＰ装置を使用することなく、強度と透光性が共に優れ、かつ直線光透過率が優れたジルコニア焼結体、このようなジルコニア焼結体を与えることのできるジルコニア成形体およびジルコニア仮焼体を提供する。本発明は、イットリアを２．０～９．０ｍｏｌ％含み、平均一次粒子径が６０ｎｍ以下で、かつ１００ｎｍを超える粒径を有する粒子が０．５質量％以下であるジルコニア粒子からなり、厚さ１．５ｍｍにおけるΔＬ＊（Ｗ－Ｂ）が５以上である、ジルコニア成形体。また、イットリアを２．０～９．０ｍｏｌ％含み、厚さ１．５ｍｍにおけるΔＬ＊（Ｗ－Ｂ）が５以上である、ジルコニア仮焼体。さらに、蛍光剤と、２．０～９．０ｍｏｌ％のイットリアを含み、厚さ１．０ｍｍにおける直線光透過率が１％以上である、ジルコニア焼結体に関する。
ZIRCONIA SINTERED COMPACT HAVING HIGH LINEAR LIGHT TRANSMITTANCE
CORPS FRITTÉ EN ZIRCONE AYANT UNE TRANSMITTANCE DE LUMIÈRE LINÉAIRE ÉLEVÉE
高い直線光透過率を有するジルコニア焼結体
KUDO YASUTAKA (author)
2020-09-10
Patent
Electronic Resource
Japanese
ZIRCONIA SINTERED COMPACT HAVING HIGH LINEAR LIGHT TRANSMITTANCE
| European Patent Office | 2022
ZIRCONIA SINTERED COMPACT HAVING HIGH LINEAR LIGHT TRANSMITTANCE
| European Patent Office | 2021
ZIRCONIA SINTERED BODY HAVING HIGH LINEAR LIGHT TRANSMITTANCE
| European Patent Office | 2022
Zirconia sintered body having high linear light transmittance
| European Patent Office | 2024
ZIRCONIA CALCINED COMPACT, ZIRCONIA SINTERED COMPACT AND LAMINATE
| European Patent Office | 2021