HIGH WHITENESS MGO SUBSTRATE, PREPARATION METHOD THEREFOR, AND DECORATIVE PLATE HAVING THE SUBSTRATE
A high whiteness MGO substrate, a preparation method therefor, and a decorative plate having the substrate. A high whiteness MGO substrate, comprising a surface layer and a substrate. The substrate consists of a forming agent, a lightweight filler, a modifier and water. The parts by mass of each component are as follows: 40-49 parts of light calcined magnesia powder, 18-25 parts of magnesium sulfate heptahydrate, 16-25 parts of a polyvinyl alcohol solution, 16-20 parts of plant powder, and 0.5-2 parts of a modifier. The modifier is formed by mixing citric acid, phosphoric acid, and sodium sulphate in a mass ratio of 10: 3: 6, and has the advantages of high internal bond strength and being not easy to peel and crack. A preparation method for the substrate has the advantages of simple preparation process, effective improvement of the internal bonding strength of the substrate, and resistance to peeling and cracking. The decorative plate has the advantages of wide application range and good applicability.
Substrat MGO à blancheur élevée, son procédé de préparation, et plaque décorative dotée du substrat. Substrat MGO à blancheur élevée, comprenant une couche de surface et un substrat. Le substrat est constitué d'un agent de formation, d'une charge légère, d'un modificateur et d'eau. Les parties en masse de chaque composant sont les suivantes : 40 à 49 parties de poudre de magnésie calcinée à la lumière, 18 à 25 parties d'heptahydrate de sulfate de magnésium, 16 à 25 parties d'une solution d'alcool polyvinylique, 16 à 20 parties de poudre végétale et 0,5 à 2 parties d'un modificateur. Le modificateur est formé par mélange d'acide citrique, d'acide phosphorique et de sulfate de sodium dans un rapport massique de 10:3:6, et présente les avantages d'une résistance de liaison interne élevée et n'est pas facile à décoller et à craquer. Un procédé de préparation du substrat présente les avantages d'un procédé de préparation simple, d'une amélioration efficace de la force de liaison interne du substrat, et d'une résistance au décollage et au craquage. La plaque décorative présente les avantages d'une large plage d'applications et d'une bonne applicabilité.
一种高白度MGO基板、制备方法及具有该基板的装饰板。一种高白度MGO基板包括面层和基板，基板由成型剂、轻质填料、改性剂和水组成，各组分的质量份如下：轻烧氧化镁粉40-49份、七水硫酸镁18-25份、聚乙烯醇溶液16-25份、植物粉体16-20份、改性剂0.5-2份；改性剂为柠檬酸：磷酸：硫酸钠按质量比为10:3:6的比例混合而成；其具有内部结合强度较高，不易剥离开裂优点；本基板的制备方法具有制备过程简单，有效改善基板的内结合强度，不易剥离开裂优点；本装饰板应用范围广，实用性好的优点。
HIGH WHITENESS MGO SUBSTRATE, PREPARATION METHOD THEREFOR, AND DECORATIVE PLATE HAVING THE SUBSTRATE
A high whiteness MGO substrate, a preparation method therefor, and a decorative plate having the substrate. A high whiteness MGO substrate, comprising a surface layer and a substrate. The substrate consists of a forming agent, a lightweight filler, a modifier and water. The parts by mass of each component are as follows: 40-49 parts of light calcined magnesia powder, 18-25 parts of magnesium sulfate heptahydrate, 16-25 parts of a polyvinyl alcohol solution, 16-20 parts of plant powder, and 0.5-2 parts of a modifier. The modifier is formed by mixing citric acid, phosphoric acid, and sodium sulphate in a mass ratio of 10: 3: 6, and has the advantages of high internal bond strength and being not easy to peel and crack. A preparation method for the substrate has the advantages of simple preparation process, effective improvement of the internal bonding strength of the substrate, and resistance to peeling and cracking. The decorative plate has the advantages of wide application range and good applicability.
Substrat MGO à blancheur élevée, son procédé de préparation, et plaque décorative dotée du substrat. Substrat MGO à blancheur élevée, comprenant une couche de surface et un substrat. Le substrat est constitué d'un agent de formation, d'une charge légère, d'un modificateur et d'eau. Les parties en masse de chaque composant sont les suivantes : 40 à 49 parties de poudre de magnésie calcinée à la lumière, 18 à 25 parties d'heptahydrate de sulfate de magnésium, 16 à 25 parties d'une solution d'alcool polyvinylique, 16 à 20 parties de poudre végétale et 0,5 à 2 parties d'un modificateur. Le modificateur est formé par mélange d'acide citrique, d'acide phosphorique et de sulfate de sodium dans un rapport massique de 10:3:6, et présente les avantages d'une résistance de liaison interne élevée et n'est pas facile à décoller et à craquer. Un procédé de préparation du substrat présente les avantages d'un procédé de préparation simple, d'une amélioration efficace de la force de liaison interne du substrat, et d'une résistance au décollage et au craquage. La plaque décorative présente les avantages d'une large plage d'applications et d'une bonne applicabilité.
一种高白度MGO基板、制备方法及具有该基板的装饰板。一种高白度MGO基板包括面层和基板，基板由成型剂、轻质填料、改性剂和水组成，各组分的质量份如下：轻烧氧化镁粉40-49份、七水硫酸镁18-25份、聚乙烯醇溶液16-25份、植物粉体16-20份、改性剂0.5-2份；改性剂为柠檬酸：磷酸：硫酸钠按质量比为10:3:6的比例混合而成；其具有内部结合强度较高，不易剥离开裂优点；本基板的制备方法具有制备过程简单，有效改善基板的内结合强度，不易剥离开裂优点；本装饰板应用范围广，实用性好的优点。
HIGH WHITENESS MGO SUBSTRATE, PREPARATION METHOD THEREFOR, AND DECORATIVE PLATE HAVING THE SUBSTRATE
SUBSTRAT DE MGO À BLANCHEUR ÉLEVÉE, SON PROCÉDÉ DE PRÉPARATION, ET PLAQUE DÉCORATIVE DOTÉE DU SUBSTRAT
一种高白度MGO基板、制备方法及具有该基板的装饰板
LI GUOPING (author)
2021-09-23
Patent
Electronic Resource
Chinese
IPC:
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
/
E04F
FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
,
Ausbau von Bauwerken, z.B. Treppen, Fußböden
| European Patent Office | 2024
Phosphogypsum-substrate imitation-copper decorative plate and preparation method thereof
| European Patent Office | 2015
MAGNETIC DECORATIVE SHEET PLATE MATERIAL DETACHABLE FROM SUBSTRATE
| European Patent Office | 2022
High-whiteness ceramic large plate and preparation method thereof
| European Patent Office | 2021
Preparation method of decorative plate and decorative plate
| European Patent Office | 2020