METHOD FOR PREPARING LOW-EXUDATION ELECTRO-FUSED ZIRCONIA-CORUNDUM BRICK WITH ADDED YTTRIUM OXIDE
Disclosed in the present invention is a method for preparing a low-exudation electro-fused zirconia-corundum brick with added yttrium oxide, which fully retains the original advantages of an electro-fused zirconia-corundum brick, has a simple process and can produce a product with good performance. In the present invention, yttrium oxide is innovatively introduced into an electro-fused zirconia-corundum brick, and same is not only introduced into a raw material, but is also coated on a surface of finished products, and industrial alumina and magnesium oxide are added to the components of raw materials, and the purity and content of zirconium oxide are improved, the initial precipitation temperature of a glass phase is greatly increased, a glass phase produced in the production of a high borosilicate glass rarely precipitates, the clarity of the produced high borosilicate glass is increased, and problems such as cracking, corrosion, and pollution of glass during production are solved, which is more beneficial to the production of medium and high borosilicate glass.
La présente invention concerne un procédé de préparation d'une brique de zircone-corindon électrofondue à faible exsudation avec ajout d'oxyde d'yttrium, qui conserve pleinement les avantages originaux d'une brique de zircone-corindon électrofondue, présente un processus simple et peut produire un produit ayant de bonnes performances. Dans la présente invention, l'oxyde d'yttrium est introduit de manière innovante dans une brique de zircone-corindon électrofondue, et celui-ci n'est pas seulement introduit dans une matière première, mais est également appliqué en revêtement sur une surface de produits finis, et de l'alumine industrielle et de l'oxyde de magnésium sont ajoutés aux composants des matières premières, et la pureté et la teneur en oxyde de zirconium sont améliorées. La température de précipitation initiale d'une phase de verre est considérablement augmentée, une phase de verre produite dans la production d'un verre à haute teneur en borosilicate précipite rarement, la clarté du verre à haute teneur en borosilicate produit est augmentée et les problèmes tels que la fissuration, la corrosion et la pollution du verre pendant la production sont résolus, ce qui est plus avantageux pour la production de verre à moyenne et haute teneur en borosilicate.
本发明公开了提供一种加入氧化钇的低渗出电熔锆刚玉砖的制备方法，充分保留了电熔锆刚玉砖原有的优点，工艺简单，且能生产出具有良好性能的产品。本发明创新地在电熔锆刚玉砖中引入了氧化钇，不仅在原始料中引入，更是在成品的表面涂抹氧化钇涂层，并在原料成分中加入工业氧化铝和氧化镁，并且提高了氧化锆的纯度和含量，极大地提高了玻璃相的初析温度，在高硼硅玻璃的生产中产生的玻璃相极少析出，增加了所生产高硼硅玻璃清晰度，解决了生产中易出现裂开、被腐蚀、易污染玻璃等问题，更利于中高硼硅玻璃的生产。
METHOD FOR PREPARING LOW-EXUDATION ELECTRO-FUSED ZIRCONIA-CORUNDUM BRICK WITH ADDED YTTRIUM OXIDE
Disclosed in the present invention is a method for preparing a low-exudation electro-fused zirconia-corundum brick with added yttrium oxide, which fully retains the original advantages of an electro-fused zirconia-corundum brick, has a simple process and can produce a product with good performance. In the present invention, yttrium oxide is innovatively introduced into an electro-fused zirconia-corundum brick, and same is not only introduced into a raw material, but is also coated on a surface of finished products, and industrial alumina and magnesium oxide are added to the components of raw materials, and the purity and content of zirconium oxide are improved, the initial precipitation temperature of a glass phase is greatly increased, a glass phase produced in the production of a high borosilicate glass rarely precipitates, the clarity of the produced high borosilicate glass is increased, and problems such as cracking, corrosion, and pollution of glass during production are solved, which is more beneficial to the production of medium and high borosilicate glass.
La présente invention concerne un procédé de préparation d'une brique de zircone-corindon électrofondue à faible exsudation avec ajout d'oxyde d'yttrium, qui conserve pleinement les avantages originaux d'une brique de zircone-corindon électrofondue, présente un processus simple et peut produire un produit ayant de bonnes performances. Dans la présente invention, l'oxyde d'yttrium est introduit de manière innovante dans une brique de zircone-corindon électrofondue, et celui-ci n'est pas seulement introduit dans une matière première, mais est également appliqué en revêtement sur une surface de produits finis, et de l'alumine industrielle et de l'oxyde de magnésium sont ajoutés aux composants des matières premières, et la pureté et la teneur en oxyde de zirconium sont améliorées. La température de précipitation initiale d'une phase de verre est considérablement augmentée, une phase de verre produite dans la production d'un verre à haute teneur en borosilicate précipite rarement, la clarté du verre à haute teneur en borosilicate produit est augmentée et les problèmes tels que la fissuration, la corrosion et la pollution du verre pendant la production sont résolus, ce qui est plus avantageux pour la production de verre à moyenne et haute teneur en borosilicate.
本发明公开了提供一种加入氧化钇的低渗出电熔锆刚玉砖的制备方法，充分保留了电熔锆刚玉砖原有的优点，工艺简单，且能生产出具有良好性能的产品。本发明创新地在电熔锆刚玉砖中引入了氧化钇，不仅在原始料中引入，更是在成品的表面涂抹氧化钇涂层，并在原料成分中加入工业氧化铝和氧化镁，并且提高了氧化锆的纯度和含量，极大地提高了玻璃相的初析温度，在高硼硅玻璃的生产中产生的玻璃相极少析出，增加了所生产高硼硅玻璃清晰度，解决了生产中易出现裂开、被腐蚀、易污染玻璃等问题，更利于中高硼硅玻璃的生产。
METHOD FOR PREPARING LOW-EXUDATION ELECTRO-FUSED ZIRCONIA-CORUNDUM BRICK WITH ADDED YTTRIUM OXIDE
PROCÉDÉ DE PRÉPARATION D'UNE BRIQUE DE ZIRCONE-CORINDON ÉLECTROFONDUE À FAIBLE EXSUDATION AVEC AJOUT D'OXYDE D'YTTRIUM
一种加入氧化钇的低渗出电熔锆刚玉砖的制备方法
WANG LI (author) / JIANG KANG (author) / CHENG BAIXUE (author) / ZHANG KUN (author) / JING CHENGGONG (author) / CHAI YUE (author) / HE XIN (author)
2022-11-03
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Fused zirconia corundum low-seepage brick production method
| European Patent Office | 2015
| European Patent Office | 2023
Production process and production equipment of high-stability fused cast zirconia-corundum brick
| European Patent Office | 2020
| European Patent Office | 2020