The invention provides a light diatomite plate. The light diatomite plate is prepared from the following raw materials in parts by weight: 30 to 40 parts of diatomite, 15 to 20 parts of cement, 10 to 15 parts of fly ash, 8 to 12 parts of resin, 5 to 10 parts of lignin fiber, 2 to 3 parts of polyethylene wax, 0.1 to 0.3 part of lime, 0.1 to 0.2 part of dispersible latex powder, 0.08 to 0.12 part of foamed aluminum powder and 0.05 to 0.1 part of gypsum. Diatomite with a special structure is used as a raw material, cement, fly ash, resin and the like are used as gelling agents, aluminum powder foaming is carried out, and a vacuum extrusion molding process is used for replacing a traditional slurry flowing method process; the light diatomite plate which is higher in breaking strength and better in durability and can better meet high-standard requirements in the fields of indoor decoration, environmental protection, energy conservation and the like is obtained after stirring, crushing, vacuum pugging and extrusion.
本发明提供一种轻质硅藻土板，包括以下重量份原料：硅藻土30‑40份，水泥15‑20份，粉煤灰10‑15份，树脂8‑12份，木质素纤维5‑10份，聚乙烯蜡2‑3份，白灰0.1‑0.3份，可分散性乳胶粉0.1‑0.2份，发泡铝粉0.08‑0.12份，石膏0.05‑0.1份。利用具有特殊结构的硅藻土为原料，利用水泥、粉煤灰、树脂等作为胶凝剂，通过进行铝粉发泡，利用真空挤出成型工艺代替传统的流浆法工艺，经搅拌粉碎、真空练泥挤出后获得抗折强度更高、耐久性更好、能更好满足室内装修、环保、节能等领域高标准要求的轻质硅藻土板。
The invention provides a light diatomite plate. The light diatomite plate is prepared from the following raw materials in parts by weight: 30 to 40 parts of diatomite, 15 to 20 parts of cement, 10 to 15 parts of fly ash, 8 to 12 parts of resin, 5 to 10 parts of lignin fiber, 2 to 3 parts of polyethylene wax, 0.1 to 0.3 part of lime, 0.1 to 0.2 part of dispersible latex powder, 0.08 to 0.12 part of foamed aluminum powder and 0.05 to 0.1 part of gypsum. Diatomite with a special structure is used as a raw material, cement, fly ash, resin and the like are used as gelling agents, aluminum powder foaming is carried out, and a vacuum extrusion molding process is used for replacing a traditional slurry flowing method process; the light diatomite plate which is higher in breaking strength and better in durability and can better meet high-standard requirements in the fields of indoor decoration, environmental protection, energy conservation and the like is obtained after stirring, crushing, vacuum pugging and extrusion.
本发明提供一种轻质硅藻土板，包括以下重量份原料：硅藻土30‑40份，水泥15‑20份，粉煤灰10‑15份，树脂8‑12份，木质素纤维5‑10份，聚乙烯蜡2‑3份，白灰0.1‑0.3份，可分散性乳胶粉0.1‑0.2份，发泡铝粉0.08‑0.12份，石膏0.05‑0.1份。利用具有特殊结构的硅藻土为原料，利用水泥、粉煤灰、树脂等作为胶凝剂，通过进行铝粉发泡，利用真空挤出成型工艺代替传统的流浆法工艺，经搅拌粉碎、真空练泥挤出后获得抗折强度更高、耐久性更好、能更好满足室内装修、环保、节能等领域高标准要求的轻质硅藻土板。
Light diatomite plate and preparation method thereof
一种轻质硅藻土板及其制备方法
03.05.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
B28C
Tonaufbereitung
,
PREPARING CLAY
Light-weight diatomite plate and preparation method thereof
| Europäisches Patentamt | 2015
Lightweight heat-insulation diatomite heat-preservation plate and preparation method thereof
| Europäisches Patentamt | 2024
Light-cured diatomite ceramic paste material and preparation method thereof
| Europäisches Patentamt | 2020