    The invention relates to a glass solder for connecting aluminum nitride ceramics as well as a preparation method and application of the glass solder. The glass solder for connecting the aluminum nitride ceramics comprises the following chemical components in percentage by weight: 60 to 65 percent of ZnO, 20 to 25 percent of B2O3, 10 to 13 percent of SiO2 and 2 to 5 percent of Al2O3, wherein the sum of the mass percentages of the components is 100 percent.

    本发明涉及一种连接氮化铝陶瓷用玻璃焊料及其制备方法和应用。所述连接氮化铝陶瓷的玻璃焊料的化学组成包括：60～65wt.％ZnO、20～25wt.％B2O3、10～13wt.％SiO2和2～5wt.％Al2O3，各组分质量百分比之和为100wt％。

    Zugriff

    Download

    Zugriff

    Download

    Seitennavigation

    Dokumentinformationen
    Ähnliche Titel

    Exportieren, teilen und zitieren

    Glass solder for connecting aluminum nitride ceramics as well as preparation method and application of glass solder

    Neue Suche nach: LIU YAN
    Neue Suche nach: WANG BO
    Neue Suche nach: LIU XUEJIAN
    Neue Suche nach: HUANG ZHENGREN

    The invention relates to a glass solder for connecting aluminum nitride ceramics as well as a preparation method and application of the glass solder. The glass solder for connecting the aluminum nitride ceramics comprises the following chemical components in percentage by weight: 60 to 65 percent of ZnO, 20 to 25 percent of B2O3, 10 to 13 percent of SiO2 and 2 to 5 percent of Al2O3, wherein the sum of the mass percentages of the components is 100 percent.

    本发明涉及一种连接氮化铝陶瓷用玻璃焊料及其制备方法和应用。所述连接氮化铝陶瓷的玻璃焊料的化学组成包括：60～65wt.％ZnO、20～25wt.％B2O3、10～13wt.％SiO2和2～5wt.％Al2O3，各组分质量百分比之和为100wt％。

    Zugriff

    Download

    Glass solder for connecting aluminum nitride ceramics as well as preparation method and application of glass solder

    Neue Suche nach: LIU YAN
    Neue Suche nach: WANG BO
    Neue Suche nach: LIU XUEJIAN
    Neue Suche nach: HUANG ZHENGREN

    The invention relates to a glass solder for connecting aluminum nitride ceramics as well as a preparation method and application of the glass solder. The glass solder for connecting the aluminum nitride ceramics comprises the following chemical components in percentage by weight: 60 to 65 percent of ZnO, 20 to 25 percent of B2O3, 10 to 13 percent of SiO2 and 2 to 5 percent of Al2O3, wherein the sum of the mass percentages of the components is 100 percent.

    本发明涉及一种连接氮化铝陶瓷用玻璃焊料及其制备方法和应用。所述连接氮化铝陶瓷的玻璃焊料的化学组成包括：60～65wt.％ZnO、20～25wt.％B2O3、10～13wt.％SiO2和2～5wt.％Al2O3，各组分质量百分比之和为100wt％。

    Zugriff

    Download

    Zugriff

    Download

    Seitennavigation

    Dokumentinformationen
    Ähnliche Titel

    Exportieren, teilen und zitieren

    Dokumentinformationen
    Titel:

    Glass solder for connecting aluminum nitride ceramics as well as preparation method and application of glass solder

    Weitere Titelangaben:

    一种连接氮化铝陶瓷用玻璃焊料及其制备方法和应用

    Beteiligte:

    LIU YAN (Autor:in) / WANG BO (Autor:in) / LIU XUEJIAN (Autor:in) / HUANG ZHENGREN (Autor:in)

    Erscheinungsdatum:

    05.11.2024

    Medientyp:

    Patent

    Format:

    Elektronische Ressource

    Sprache:

    Chinesisch

    Klassifikation:

    IPC:  C03C Chemische Zusammensetzungen für Gläser, Glasuren oder Emails , CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS / C04B Kalk , LIME / H01L Halbleiterbauelemente , SEMICONDUCTOR DEVICES

    Ähnliche Titel

    Microcrystalline glass solder and preparation method thereof, and method for connecting aluminum oxide ceramics

    LI KAI / WAN DETIAN / LI YUEMING et al. | Europäisches Patentamt | 2021

    Freier Zugriff

    Low-thermal-expansion-coefficient glass solder for connecting ceramics, preparation method and connecting method

    LIU YAN / PAN ZIHAO / WANG BO et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Method for connecting aluminum oxide ceramic and aluminum through composite glass solder

    FU WEI / XUE YIDI / SONG XIAOGUO et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    Method for connecting silicon nitride ceramic composite structure by using glass solder

    SUN LIANGBO / ZHANG JIE / LIU CHUNFENG et al. | Europäisches Patentamt | 2022

    Freier Zugriff

    Method for permeation connection of zirconia ceramics through glass solder

    ZHU WEIWEI / TANG MU / ZOU HAOHAO et al. | Europäisches Patentamt | 2021

    Freier Zugriff
    Nach oben