METHOD FOR PRODUCING DIAMOND-METAL CARBIDE COMPOUND SINTERED COMPACT
PROBLEM TO BE SOLVED: To provide a method for producing a diamond-metal carbide compound sintered compact having a high hardness.SOLUTION: The method for producing a diamond-metal carbide compound sintered compact includes the steps of: forming a preform containing a catalyst metal powder containing 1 or more kinds of metal selected from Co, Ni, Mn, and Fe, and a carbide-forming metal powder containing 1 or more kinds of metal selected from Ti, Nb, V, Zr, Hf, and Cr; forming a carbide of carbide-forming metal by press-sintering the preform at a first temperature with carbide forming reaction using the catalyst metal as a catalyst; and sintering the diamond by press-sintering the preform after forming the carbide at a second temperature.SELECTED DRAWING: Figure 2
【課題】高硬度のダイヤモンド−金属炭化物複合焼結体の製造方法を提供する。【解決手段】ダイヤモンド粉末と、Ｃｏ，Ｎｉ，Ｍｎ，Ｆｅから選ばれる１種以上の金属を含む触媒金属粉末と、Ｔｉ，Ｎｂ，Ｖ，Ｚｒ，Ｈｆ，Ｃｒから選ばれる１種以上の金属を含む炭化物形成金属粉末とを含むプリフォームを形成する工程と、プリフォームを第１の温度で加圧焼結することで、触媒金属を触媒とする炭化物形成反応により、炭化物形成金属の炭化物を形成する工程と、炭化物形成後のプリフォームを第２の温度で加圧焼結することにより、ダイヤモンドを焼結する工程と、を含むダイヤモンド−金属炭化物複合焼結体の製造方法。【選択図】図２
METHOD FOR PRODUCING DIAMOND-METAL CARBIDE COMPOUND SINTERED COMPACT
PROBLEM TO BE SOLVED: To provide a method for producing a diamond-metal carbide compound sintered compact having a high hardness.SOLUTION: The method for producing a diamond-metal carbide compound sintered compact includes the steps of: forming a preform containing a catalyst metal powder containing 1 or more kinds of metal selected from Co, Ni, Mn, and Fe, and a carbide-forming metal powder containing 1 or more kinds of metal selected from Ti, Nb, V, Zr, Hf, and Cr; forming a carbide of carbide-forming metal by press-sintering the preform at a first temperature with carbide forming reaction using the catalyst metal as a catalyst; and sintering the diamond by press-sintering the preform after forming the carbide at a second temperature.SELECTED DRAWING: Figure 2
【課題】高硬度のダイヤモンド−金属炭化物複合焼結体の製造方法を提供する。【解決手段】ダイヤモンド粉末と、Ｃｏ，Ｎｉ，Ｍｎ，Ｆｅから選ばれる１種以上の金属を含む触媒金属粉末と、Ｔｉ，Ｎｂ，Ｖ，Ｚｒ，Ｈｆ，Ｃｒから選ばれる１種以上の金属を含む炭化物形成金属粉末とを含むプリフォームを形成する工程と、プリフォームを第１の温度で加圧焼結することで、触媒金属を触媒とする炭化物形成反応により、炭化物形成金属の炭化物を形成する工程と、炭化物形成後のプリフォームを第２の温度で加圧焼結することにより、ダイヤモンドを焼結する工程と、を含むダイヤモンド−金属炭化物複合焼結体の製造方法。【選択図】図２
METHOD FOR PRODUCING DIAMOND-METAL CARBIDE COMPOUND SINTERED COMPACT
ダイヤモンド−金属炭化物複合焼結体の製造方法
AHMADI EKO WARDOYO (Autor:in) / FUKUNAGA OSAMU (Autor:in) / MATSUO TOSHIHIKO (Autor:in) / SAKURAZAWA CHIHIRO (Autor:in)
24.11.2016
Patent
Elektronische Ressource
Japanisch
| Europäisches Patentamt | 2024
METHOD FOR PRODUCING SILICON CARBIDE SINTERED COMPACT
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2015
SINTERED COMPACT OF SILICON CARBIDE AND PRODUCING METHOD THEREOF
| Europäisches Patentamt | 2015