Torpedo ladle lining repairing sprayed material as well as preparation method and use method thereof
The invention provides a torpedo ladle lining repairing sprayed material which comprises the following raw materials in percentage by mass: 35-45% of waste torpedo ladle bricks, 20-25% of brown fused alumina, 12-18% of silicon carbide powder, 10-15% of waste iron runner material powder, 4-6% of pure calcium aluminate cement, 3-5% of an additive, 0.5-1.5% of an antioxidant as well as a water reducing agent which accounts for 0.1-0.5% of the total amount of the spraying material, and an anti-explosion agent which accounts for 0.02-0.05% of the total amount of the sprayed material. The preparation method of the sprayed material comprises the following steps: uniformly mixing the raw materials in a strong stirring machine for 2-4 minutes according to the ratio, thereby obtaining the spraying material. The use method of the spraying material comprises the following steps: adding water which accounts for 5-7wt.% of the total mass of the spraying material, uniformly mixing for 1-2 minutes in the strong stirring machine, spraying, and drying for 2-3 hours at 500-700 DEG C, thereby normally using a torpedo ladle. When the sprayed material is used, the service life of the torpedo ladle can be prolonged by 10% or above, and as waste materials are used as a main raw material, the production and use cost can be greatly lowered and the environment can be protected.
Torpedo ladle lining repairing sprayed material as well as preparation method and use method thereof
The invention provides a torpedo ladle lining repairing sprayed material which comprises the following raw materials in percentage by mass: 35-45% of waste torpedo ladle bricks, 20-25% of brown fused alumina, 12-18% of silicon carbide powder, 10-15% of waste iron runner material powder, 4-6% of pure calcium aluminate cement, 3-5% of an additive, 0.5-1.5% of an antioxidant as well as a water reducing agent which accounts for 0.1-0.5% of the total amount of the spraying material, and an anti-explosion agent which accounts for 0.02-0.05% of the total amount of the sprayed material. The preparation method of the sprayed material comprises the following steps: uniformly mixing the raw materials in a strong stirring machine for 2-4 minutes according to the ratio, thereby obtaining the spraying material. The use method of the spraying material comprises the following steps: adding water which accounts for 5-7wt.% of the total mass of the spraying material, uniformly mixing for 1-2 minutes in the strong stirring machine, spraying, and drying for 2-3 hours at 500-700 DEG C, thereby normally using a torpedo ladle. When the sprayed material is used, the service life of the torpedo ladle can be prolonged by 10% or above, and as waste materials are used as a main raw material, the production and use cost can be greatly lowered and the environment can be protected.
Torpedo ladle lining repairing sprayed material as well as preparation method and use method thereof
ZHU JICHANG (author) / ZUO LIANGZHU (author) / FAN LINGJIANG (author) / TIAN SHIJIN (author) / TIAN SHIXIU (author)
2015-07-01
Patent
Electronic Resource
English
Torpedo ladle lining smearing repair material, preparation method and use method
European Patent Office | 2020
|Coating material for iron ladle and torpedo ladle and preparation method of coating material
European Patent Office | 2022
|Ladle working lining castable, ladle working lining and preparation method of ladle working lining
European Patent Office | 2023
|