The invention relates to the field of concrete blocks, in particular to a production process of ceramsite aerated concrete blocks, which comprises the following steps: raw material preparation: respectively grinding fly ash, slag and coal cinder, and then weighing the raw materials according to the formula; stirring: adding the weighed cement, fly ash, ceramsite, slag, coal cinder and water reducing agent into a stirrer, and stirring and mixing in advance; foaming: adding the foaming agent, the exciting agent, the coagulating and hardening accelerator and the water which are weighed into the stirrer, and fully stirring and mixing to form a viscous mixture; preparing a building block mold; pouring is conducted; hardening is conducted; demolding to obtain a green body; performing cutting; performing maintenance; and detecting whether the product is qualified or not. The ceramsite is added into the building block material, so that the building block has the characteristics of light weight, heat insulation, fire prevention, sound insulation, environmental protection and the like, the material performance of a wall is improved, the fly ash, the slag and the coal cinder are pre-ground, the surface area of the raw materials is increased, the mixture is easier to mix uniformly, and the quality of the building block is improved.
本申请涉及混凝土砌块的领域，尤其是一种陶粒加气混凝土砌块的生产工艺，其包括以下步骤，原料准备，将粉煤灰、矿渣和煤渣分别进行研磨，再按照配方对原料进行称量；搅拌，把称重好的水泥、粉煤灰、陶粒、矿渣、煤渣和减水剂加入搅拌机内进行预先搅拌混合；发泡，把称重好的发泡剂、激发剂、促凝促硬剂和水再加入搅拌机内进行充分搅拌混合，形成粘稠状混合物；准备砌块模具；浇注；硬化；脱模，得到坯体；切割；养护；检测，检测产品是否合格。在砌块材料内加入陶粒，使得砌块具有轻质、隔热保温、防火、隔音、环保等特点，提高墙体的材料性能，将粉煤灰、矿渣和煤渣预先研磨，增大原料表面积，使得混合物更容易混合均匀，提高砌块质量。
Production process of ceramsite aerated concrete block
The invention relates to the field of concrete blocks, in particular to a production process of ceramsite aerated concrete blocks, which comprises the following steps: raw material preparation: respectively grinding fly ash, slag and coal cinder, and then weighing the raw materials according to the formula; stirring: adding the weighed cement, fly ash, ceramsite, slag, coal cinder and water reducing agent into a stirrer, and stirring and mixing in advance; foaming: adding the foaming agent, the exciting agent, the coagulating and hardening accelerator and the water which are weighed into the stirrer, and fully stirring and mixing to form a viscous mixture; preparing a building block mold; pouring is conducted; hardening is conducted; demolding to obtain a green body; performing cutting; performing maintenance; and detecting whether the product is qualified or not. The ceramsite is added into the building block material, so that the building block has the characteristics of light weight, heat insulation, fire prevention, sound insulation, environmental protection and the like, the material performance of a wall is improved, the fly ash, the slag and the coal cinder are pre-ground, the surface area of the raw materials is increased, the mixture is easier to mix uniformly, and the quality of the building block is improved.
本申请涉及混凝土砌块的领域，尤其是一种陶粒加气混凝土砌块的生产工艺，其包括以下步骤，原料准备，将粉煤灰、矿渣和煤渣分别进行研磨，再按照配方对原料进行称量；搅拌，把称重好的水泥、粉煤灰、陶粒、矿渣、煤渣和减水剂加入搅拌机内进行预先搅拌混合；发泡，把称重好的发泡剂、激发剂、促凝促硬剂和水再加入搅拌机内进行充分搅拌混合，形成粘稠状混合物；准备砌块模具；浇注；硬化；脱模，得到坯体；切割；养护；检测，检测产品是否合格。在砌块材料内加入陶粒，使得砌块具有轻质、隔热保温、防火、隔音、环保等特点，提高墙体的材料性能，将粉煤灰、矿渣和煤渣预先研磨，增大原料表面积，使得混合物更容易混合均匀，提高砌块质量。
Production process of ceramsite aerated concrete block
陶粒加气混凝土砌块的生产工艺
2024-04-09
Patent
Electronic Resource
Chinese
IPC:
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
B08B
Reinigen allgemein
,
CLEANING IN GENERAL
/
B28C
Tonaufbereitung
,
PREPARING CLAY
/
C04B
Kalk
,
LIME
Ceramsite aerated concrete block and production process thereof
| European Patent Office | 2022
| European Patent Office | 2023