Production method for preparing petuntse from waste porcelain powder
The invention discloses a production method for preparing petuntse from waste ceramic powder, and belongs to the technical field of ceramic materials. The method comprises the following steps: step 1, adding waste porcelain powder, albite, potassium feldspar, ball clay, high-whiteness raw ore, modified kaolin and calcined talc into a ball mill in parts by weight, adding water, and carrying out ball milling and mixing for 24-36 hours to obtain pug; and step 2, sieving the pug obtained in the step 1 to remove iron, carrying out filter pressing, and pugging to obtain the petuntse. The modified kaolin provided by the invention has relatively high dispersing performance, is not easy to agglomerate and has an excellent mixing effect. The petuntse prepared from the waste porcelain powder has high plasticity, and is not easy to crack, dry-shrink and the like in the use process; the waste ceramic powder generated in the ceramic industry is effectively utilized, the production method of the petuntse is widened, and the method has great significance in the ceramic industry.
本发明公开了一种用废瓷粉制成瓷泥的生产方法，属于陶瓷材料技术领域。上述方法包括如下步骤：步骤1、按重量份将废瓷粉、钠长石、钾长石、球土、高白原矿、改性高岭土和煅烧滑石加入球磨机中，加入水，球磨混合24‑36小时，得到泥料；步骤2、将步骤1中所得泥料过筛除铁、压滤、练泥，制得瓷泥。本发明中的改性高岭土具有较高的分散性能，不易发生团聚现象，混合效果优异。本发明中利用废瓷粉制成的瓷泥具有高塑性，在使用过程中不易发生开裂，干缩等现象；本发明不仅对陶瓷工业产生的废瓷粉进行了有效地利用，且拓宽了瓷泥的生产方法，对陶瓷工业具有重大的意义。
Production method for preparing petuntse from waste porcelain powder
The invention discloses a production method for preparing petuntse from waste ceramic powder, and belongs to the technical field of ceramic materials. The method comprises the following steps: step 1, adding waste porcelain powder, albite, potassium feldspar, ball clay, high-whiteness raw ore, modified kaolin and calcined talc into a ball mill in parts by weight, adding water, and carrying out ball milling and mixing for 24-36 hours to obtain pug; and step 2, sieving the pug obtained in the step 1 to remove iron, carrying out filter pressing, and pugging to obtain the petuntse. The modified kaolin provided by the invention has relatively high dispersing performance, is not easy to agglomerate and has an excellent mixing effect. The petuntse prepared from the waste porcelain powder has high plasticity, and is not easy to crack, dry-shrink and the like in the use process; the waste ceramic powder generated in the ceramic industry is effectively utilized, the production method of the petuntse is widened, and the method has great significance in the ceramic industry.
本发明公开了一种用废瓷粉制成瓷泥的生产方法，属于陶瓷材料技术领域。上述方法包括如下步骤：步骤1、按重量份将废瓷粉、钠长石、钾长石、球土、高白原矿、改性高岭土和煅烧滑石加入球磨机中，加入水，球磨混合24‑36小时，得到泥料；步骤2、将步骤1中所得泥料过筛除铁、压滤、练泥，制得瓷泥。本发明中的改性高岭土具有较高的分散性能，不易发生团聚现象，混合效果优异。本发明中利用废瓷粉制成的瓷泥具有高塑性，在使用过程中不易发生开裂，干缩等现象；本发明不仅对陶瓷工业产生的废瓷粉进行了有效地利用，且拓宽了瓷泥的生产方法，对陶瓷工业具有重大的意义。
Production method for preparing petuntse from waste porcelain powder
一种用废瓷粉制成瓷泥的生产方法
ZHOU HENG (author) / LI ZHIXING (author) / LI HANG (author) / XIE ZHILAI (author) / LUO JIECHUN (author)
2024-06-04
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2022
Process method for preparing soft porcelain from PC solid waste
| European Patent Office | 2021
Porcelain glazed brick prepared from waste materials and production method of porcelain glazed brick
| European Patent Office | 2021
Colored porcelain prepared from waste porcelain and preparation method of same
| European Patent Office | 2020