MANUFACTURING METHOD FOR GROUTING CHEMICAL LIQUID AGENCY
The present invention relates to a method for producing a grouting liquid chemical composition and more specifically, to a method for producing a grouting liquid chemical composition that uses no or a minimal amount of type I normal cement by using a desulfurization by-product generated by combustion of petroleum coke and slag. The method for producing a grouting liquid chemical composition according to the present invention includes: 1) diluting liquid soda silicate with water to obtain a solution A; 2) obtaining a binder containing 1 to 500 parts by weight of a desulfurization by-product generated by combustion of petroleum coke, the desulfurization by-product having a calcium oxide content of 50 to 80 wt%, a sulfate oxide content of 10 to 40 wt% and a specific surface area of 2,000 to 8,000 cm^2/g with respect to 100 parts by weight of slag having a calcium oxide content of 30 to 70 wt% and a specific surface area of 3,500 to 8,000 cm^2/g; 3) mixing the binder with water to obtain a solution B; and 4) mixing the solution A with the solution B, followed by gelling.
본 발명은 그라우팅 약액 조성물 제조방법에 관한 것으로서, 보다 상세하게는 페트로 코크스 연소시 발생되는 탈황 부산물과 슬래그를 이용함으로써 1종 보통시멘트를 전혀 사용하지 않거나 그 사용량을 최소화할 수 있는 그라우팅 약액 조성물 제조방법에 관한 것이다. 본 발명에 의한 그라우팅 약액 조성물 제조방법은 1) 액상 규산소다를 물로 희석시켜 A액을 얻는 단계; 2) 칼슘 옥사이드(Calcium oxide) 함량이 30~70중량%이고 비표면적이 3,500~8,000cm/g인 슬래그 100중량부에 대하여, 칼슘 옥사이드(Calcium oxide) 함량이 50~80중량%이고 설페이트 옥사이드(Sulfate oxide) 함량이 10~40중량%이며 비표면적이 2,000~8,000cm/g인 페트로 코크스 연소시 발생되는 탈황 부산물 1~500중량부를 포함하는 결합재를 얻는 단계; 3) 상기 결합재에 물을 혼합하여 B액을 얻는 단계; 및 4) 상기 A액과 B액을 혼합하여 겔(gel)화 시키는 단계;를 포함한다.
MANUFACTURING METHOD FOR GROUTING CHEMICAL LIQUID AGENCY
The present invention relates to a method for producing a grouting liquid chemical composition and more specifically, to a method for producing a grouting liquid chemical composition that uses no or a minimal amount of type I normal cement by using a desulfurization by-product generated by combustion of petroleum coke and slag. The method for producing a grouting liquid chemical composition according to the present invention includes: 1) diluting liquid soda silicate with water to obtain a solution A; 2) obtaining a binder containing 1 to 500 parts by weight of a desulfurization by-product generated by combustion of petroleum coke, the desulfurization by-product having a calcium oxide content of 50 to 80 wt%, a sulfate oxide content of 10 to 40 wt% and a specific surface area of 2,000 to 8,000 cm^2/g with respect to 100 parts by weight of slag having a calcium oxide content of 30 to 70 wt% and a specific surface area of 3,500 to 8,000 cm^2/g; 3) mixing the binder with water to obtain a solution B; and 4) mixing the solution A with the solution B, followed by gelling.
본 발명은 그라우팅 약액 조성물 제조방법에 관한 것으로서, 보다 상세하게는 페트로 코크스 연소시 발생되는 탈황 부산물과 슬래그를 이용함으로써 1종 보통시멘트를 전혀 사용하지 않거나 그 사용량을 최소화할 수 있는 그라우팅 약액 조성물 제조방법에 관한 것이다. 본 발명에 의한 그라우팅 약액 조성물 제조방법은 1) 액상 규산소다를 물로 희석시켜 A액을 얻는 단계; 2) 칼슘 옥사이드(Calcium oxide) 함량이 30~70중량%이고 비표면적이 3,500~8,000cm/g인 슬래그 100중량부에 대하여, 칼슘 옥사이드(Calcium oxide) 함량이 50~80중량%이고 설페이트 옥사이드(Sulfate oxide) 함량이 10~40중량%이며 비표면적이 2,000~8,000cm/g인 페트로 코크스 연소시 발생되는 탈황 부산물 1~500중량부를 포함하는 결합재를 얻는 단계; 3) 상기 결합재에 물을 혼합하여 B액을 얻는 단계; 및 4) 상기 A액과 B액을 혼합하여 겔(gel)화 시키는 단계;를 포함한다.
MANUFACTURING METHOD FOR GROUTING CHEMICAL LIQUID AGENCY
그라우팅 약액 조성물 제조방법
MUN GYOUNG JU (author) / YOON SEONG JIN (author)
2016-02-24
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
MANUFACTURING METHOD FOR GROUTING CHEMICAL LIQUID AGENCY
| European Patent Office | 2016
GROUTING COMPONENTS WITH BLAST FURNACE SLAG AND GROUTING CHEMICAL LIQUID AGENCY USING IT
| European Patent Office | 2017
Preparing method for environment-friendly silicate chemical grouting liquid and grouting gel
| European Patent Office | 2015