METHOD FOR PRODUCING AQUEOUS SYNTHETIC RESIN EMULSION, METHOD FOR PRODUCING REEMULSIFIABLE SYNTHETIC RESIN POWDER, METHOD FOR PRODUCING POLYMER CEMENT MORTAR, AQUEOUS SYNTHETIC RESIN EMULSION, AND REEMULSIFIABLE SYNTHETIC RESIN POWDER
Provided is a method for producing an aqueous synthetic resin emulsion having a high solids fraction concentration and low viscosity with which it is possible to obtain a reemulsifiable synthetic resin powder having excellent workability after reemulsification. A method for producing an aqueous synthetic resin emulsion for emulsion polymerizing a polymerization component [1] in the presence of a polyvinyl alcohol resin, wherein the method for producing an aqueous synthetic resin emulsion contains a hydrophobic monomer having a solubility in 20°C water of 0.1% or less in a quantity of 30 wt% or more relative to the entire polymerization component [1] and conducts emulsion polymerization while continuously adding the total amount of polymerization component [1] in an aqueous medium.
L'invention concerne un procédé de production d'une émulsion aqueuse de résine synthétique présentant une forte concentration de fraction de solides et une faible viscosité, permettant d'obtenir une poudre de résine synthétique ré-émulsifiable ayant une excellente aptitude au façonnage après ré-émulsification. L'invention décrit un procédé de production d'une émulsion aqueuse de résine synthétique pour la polymérisation en émulsion d'un constituant de polymérisation [1] en présence d'une résine d'alcool polyvinylique, le procédé de production d'une émulsion aqueuse de résine synthétique contenant un monomère hydrophobe présentant une solubilité dans l'eau inférieure ou égale à 20 °C de 0,1 % dans une quantité supérieure ou égale à 30 % en poids par rapport à la totalité du constituant de polymérisation [1] et conduit à la polymérisation en émulsion tout en ajoutant de manière continue la quantité totale de constituant de polymérisation [1] dans un milieu aqueux.
生産効率がよく、再乳化後の作業性にも優れる再乳化性合成樹脂粉末を得ることができる、高固形分濃度かつ低粘度の水性合成樹脂エマルジョンの製造方法を提供する。重合成分［Ｉ］をポリビニルアルコール系樹脂の存在下で乳化重合する水性合成樹脂エマルジョンの製造方法であって、２０℃の水に対する溶解度が０．１％以下である疎水性モノマーを重合成分［Ｉ］全体に対して３０重量％以上含有し、水性媒体中に、重合成分［Ｉ］の全量を連続して添加しながら乳化重合することを特徴とする水性合成樹脂エマルジョンの製造方法である。
METHOD FOR PRODUCING AQUEOUS SYNTHETIC RESIN EMULSION, METHOD FOR PRODUCING REEMULSIFIABLE SYNTHETIC RESIN POWDER, METHOD FOR PRODUCING POLYMER CEMENT MORTAR, AQUEOUS SYNTHETIC RESIN EMULSION, AND REEMULSIFIABLE SYNTHETIC RESIN POWDER
Provided is a method for producing an aqueous synthetic resin emulsion having a high solids fraction concentration and low viscosity with which it is possible to obtain a reemulsifiable synthetic resin powder having excellent workability after reemulsification. A method for producing an aqueous synthetic resin emulsion for emulsion polymerizing a polymerization component [1] in the presence of a polyvinyl alcohol resin, wherein the method for producing an aqueous synthetic resin emulsion contains a hydrophobic monomer having a solubility in 20°C water of 0.1% or less in a quantity of 30 wt% or more relative to the entire polymerization component [1] and conducts emulsion polymerization while continuously adding the total amount of polymerization component [1] in an aqueous medium.
L'invention concerne un procédé de production d'une émulsion aqueuse de résine synthétique présentant une forte concentration de fraction de solides et une faible viscosité, permettant d'obtenir une poudre de résine synthétique ré-émulsifiable ayant une excellente aptitude au façonnage après ré-émulsification. L'invention décrit un procédé de production d'une émulsion aqueuse de résine synthétique pour la polymérisation en émulsion d'un constituant de polymérisation [1] en présence d'une résine d'alcool polyvinylique, le procédé de production d'une émulsion aqueuse de résine synthétique contenant un monomère hydrophobe présentant une solubilité dans l'eau inférieure ou égale à 20 °C de 0,1 % dans une quantité supérieure ou égale à 30 % en poids par rapport à la totalité du constituant de polymérisation [1] et conduit à la polymérisation en émulsion tout en ajoutant de manière continue la quantité totale de constituant de polymérisation [1] dans un milieu aqueux.
生産効率がよく、再乳化後の作業性にも優れる再乳化性合成樹脂粉末を得ることができる、高固形分濃度かつ低粘度の水性合成樹脂エマルジョンの製造方法を提供する。重合成分［Ｉ］をポリビニルアルコール系樹脂の存在下で乳化重合する水性合成樹脂エマルジョンの製造方法であって、２０℃の水に対する溶解度が０．１％以下である疎水性モノマーを重合成分［Ｉ］全体に対して３０重量％以上含有し、水性媒体中に、重合成分［Ｉ］の全量を連続して添加しながら乳化重合することを特徴とする水性合成樹脂エマルジョンの製造方法である。
METHOD FOR PRODUCING AQUEOUS SYNTHETIC RESIN EMULSION, METHOD FOR PRODUCING REEMULSIFIABLE SYNTHETIC RESIN POWDER, METHOD FOR PRODUCING POLYMER CEMENT MORTAR, AQUEOUS SYNTHETIC RESIN EMULSION, AND REEMULSIFIABLE SYNTHETIC RESIN POWDER
PROCÉDÉ DE PRODUCTION D'ÉMULSION AQUEUSE DE RÉSINE SYNTHÉTIQUE, PROCÉDÉ DE PRODUCTION DE POUDRE DE RÉSINE SYNTHÉTIQUE RÉ-ÉMULSIFIABLE, PROCÉDÉ DE PRODUCTION D'UN MORTIER DE CIMENT POLYMÈRE, ÉMULSION AQUEUSE DE RÉSINE SYNTHÉTIQUE, ET POUDRE DE RÉSINE SYNTHÉTIQUE RÉ-ÉMULSIFIABLE
水性合成樹脂エマルジョンの製造方法、再乳化性合成樹脂粉末の製造方法、ポリマーセメントモルタルの製造方法、水性合成樹脂エマルジョン及び再乳化性合成樹脂粉末
MURASE NAOKAZU (author) / AIBA KAZUO (author) / EDASAWA KATSUMI (author)
2017-06-22
Patent
Electronic Resource
Japanese
| European Patent Office | 2020
THERMOPLASTIC SYNTHETIC RESIN FLOORING AND METHOD FOR PRODUCING THE SAME
| European Patent Office | 2019
SYNTHETIC RESIN TATAMI MAT MANUFACTURING METHOD AND SYNTHETIC RESIN TATAMI MAT
| European Patent Office | 2017