LARGE CERAMIC SHEET FOR BUILDING MATERIAL USE
The purpose of the present invention is to provide a large ceramic sheet for building material use, in which efflorescence is prevented. A large ceramic sheet for building material use according to the present invention, which solves said problem, is obtained by kneading, shaping, and then sintering a starting material composition having, as the main constituents, a refractory aggregate, a glass starting material, and cement, wherein the Na2O content in the chemical components of the entire composition after sintering is 1 mass% or less. In addition, in terms of the chemical composition values based on mass, the ceramic sheet has a Na2O content of 1% or less and includes 0.5-7% BaO and 0.5-8% B2O3 (BaO+B2O3: 12% or less).
L'invention a pour objet de fournir un carreau de céramique de grande taille pour matériau de construction dont l'efflorescence est prévenue. À cet effet, ce carreau de céramique de grande taille pour matériau de construction est constitué par malaxage d'un mélange de matières de départ avec pour principaux composants un agrégat résistant au feu, une matière de départ de verre et un ciment, par moulage puis par cuisson. La teneur en Ｎａ２Ｏ est inférieure ou égale à 1% en masse dans la composition chimique de l'ensemble de la composition après cuisson. En outre, en termes de valeur de composants chimiques en masse, l'objet de l'invention présente une teneur en Ｎａ２Ｏ inférieure ou égale à 1%, et comprend ０,５ à ７％ d'un ＢａＯ, et ０,５ à ８％ d'un Ｂ２Ｏ３ （１２％ ou moins d'un ＢａＯ＋Ｂ２Ｏ３).
本発明は、白華を防止した建材用大型陶板を提供することを目的とする。 その解決手段として、本発明に係る建材用大型陶板は、耐火性骨材、ガラス質原料およびセメントを主材とした原料配合物を混練、成形後、焼成してなる建材用大型陶板であって、焼成後の組成全体の化学成分において、Ｎａ２Ｏ含有量を１質量％以下としている。また、質量基準による化学成分値で、Ｎａ２Ｏ含有量を１％以下とし、かつＢａＯ：０．５～７％およびＢ２Ｏ３：０．５～８％（ＢａＯ＋Ｂ２Ｏ３：１２％以下）を含有する。
LARGE CERAMIC SHEET FOR BUILDING MATERIAL USE
The purpose of the present invention is to provide a large ceramic sheet for building material use, in which efflorescence is prevented. A large ceramic sheet for building material use according to the present invention, which solves said problem, is obtained by kneading, shaping, and then sintering a starting material composition having, as the main constituents, a refractory aggregate, a glass starting material, and cement, wherein the Na2O content in the chemical components of the entire composition after sintering is 1 mass% or less. In addition, in terms of the chemical composition values based on mass, the ceramic sheet has a Na2O content of 1% or less and includes 0.5-7% BaO and 0.5-8% B2O3 (BaO+B2O3: 12% or less).
L'invention a pour objet de fournir un carreau de céramique de grande taille pour matériau de construction dont l'efflorescence est prévenue. À cet effet, ce carreau de céramique de grande taille pour matériau de construction est constitué par malaxage d'un mélange de matières de départ avec pour principaux composants un agrégat résistant au feu, une matière de départ de verre et un ciment, par moulage puis par cuisson. La teneur en Ｎａ２Ｏ est inférieure ou égale à 1% en masse dans la composition chimique de l'ensemble de la composition après cuisson. En outre, en termes de valeur de composants chimiques en masse, l'objet de l'invention présente une teneur en Ｎａ２Ｏ inférieure ou égale à 1%, et comprend ０,５ à ７％ d'un ＢａＯ, et ０,５ à ８％ d'un Ｂ２Ｏ３ （１２％ ou moins d'un ＢａＯ＋Ｂ２Ｏ３).
本発明は、白華を防止した建材用大型陶板を提供することを目的とする。 その解決手段として、本発明に係る建材用大型陶板は、耐火性骨材、ガラス質原料およびセメントを主材とした原料配合物を混練、成形後、焼成してなる建材用大型陶板であって、焼成後の組成全体の化学成分において、Ｎａ２Ｏ含有量を１質量％以下としている。また、質量基準による化学成分値で、Ｎａ２Ｏ含有量を１％以下とし、かつＢａＯ：０．５～７％およびＢ２Ｏ３：０．５～８％（ＢａＯ＋Ｂ２Ｏ３：１２％以下）を含有する。
LARGE CERAMIC SHEET FOR BUILDING MATERIAL USE
CARREAU DE CÉRAMIQUE DE GRANDE TAILLE POUR MATÉRIAU DE CONSTRUCTION
建材用大型陶板
FURUKAWA MASATO (author)
2021-12-30
Patent
Electronic Resource
Japanese