Concrete sealing curing agent and construction process thereof
The invention provides a concrete sealing curing agent. The concrete sealing curing agent is composed of 50-70 wt% of active silicate, 10-20 wt% of a mixture of magnesium fluosilicate and zinc fluosilicate, 1-3 wt% of hydrofluoric acid, 1-3 wt% of a polyguanidine salt, 1-3 wt% of a micro-expanding agent, and the balance of water and other assistants. The concrete permeation sealing curing agent isa colorless, odorless, non-toxic and harmless novel antibacterial building material, a polymerization solution using active silicate as a main component can be applied to renovation of a newly-pouredconcrete ground or an old ground, by sufficient permeation, the effective components can quickly undergo a chemical reaction with free calcium in the concrete so that crystal colloid is generated tofill structure gaps, the compactness of the structure is improved, a sealing entity as hard as rock is formed on the surface layer of the concrete, the strength and the wear resistance of the surfacelayer of the concrete structure are greatly improved, the ground is permanently dustproof, anti-skid, wear-resistant, hard, pressure-resistant, impermeable, weather-resistant, chemical-resistant, bright, environment-friendly and the like, and the service life of the ground is prolonged.
本发明提供了一种混凝土密封固化剂，由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成。该混凝土渗透密封固化剂是一种无色、无味、无毒、无害的新型抗菌建筑材料，以活性硅酸盐为主要成分的聚合溶液，可应用在新浇筑混凝土地面或旧地面翻新，通过充分渗透，其有效成份能迅速地与混凝土中的游离钙发生化学反应，生成结晶胶体来填充结构空隙，增加结构的致密性，使得混凝土表层形成一个坚如岩石的密封实体，极大地提高混凝土结构表层的强度和耐磨性，从而使地面永久防尘、防滑、耐磨、坚硬、抗压、抗渗、抗风化、耐化学性、光亮、环保等，延长了地面的使用寿命。
Concrete sealing curing agent and construction process thereof
The invention provides a concrete sealing curing agent. The concrete sealing curing agent is composed of 50-70 wt% of active silicate, 10-20 wt% of a mixture of magnesium fluosilicate and zinc fluosilicate, 1-3 wt% of hydrofluoric acid, 1-3 wt% of a polyguanidine salt, 1-3 wt% of a micro-expanding agent, and the balance of water and other assistants. The concrete permeation sealing curing agent isa colorless, odorless, non-toxic and harmless novel antibacterial building material, a polymerization solution using active silicate as a main component can be applied to renovation of a newly-pouredconcrete ground or an old ground, by sufficient permeation, the effective components can quickly undergo a chemical reaction with free calcium in the concrete so that crystal colloid is generated tofill structure gaps, the compactness of the structure is improved, a sealing entity as hard as rock is formed on the surface layer of the concrete, the strength and the wear resistance of the surfacelayer of the concrete structure are greatly improved, the ground is permanently dustproof, anti-skid, wear-resistant, hard, pressure-resistant, impermeable, weather-resistant, chemical-resistant, bright, environment-friendly and the like, and the service life of the ground is prolonged.
本发明提供了一种混凝土密封固化剂，由50～70wt％的活性硅酸盐、10～20wt％的氟硅酸镁与氟硅酸锌的混合物、1～3wt％的氢氟酸、1～3wt％的聚和胍盐、1～3wt％的微膨胀剂、其余为水和其他助剂组成。该混凝土渗透密封固化剂是一种无色、无味、无毒、无害的新型抗菌建筑材料，以活性硅酸盐为主要成分的聚合溶液，可应用在新浇筑混凝土地面或旧地面翻新，通过充分渗透，其有效成份能迅速地与混凝土中的游离钙发生化学反应，生成结晶胶体来填充结构空隙，增加结构的致密性，使得混凝土表层形成一个坚如岩石的密封实体，极大地提高混凝土结构表层的强度和耐磨性，从而使地面永久防尘、防滑、耐磨、坚硬、抗压、抗渗、抗风化、耐化学性、光亮、环保等，延长了地面的使用寿命。
Concrete sealing curing agent and construction process thereof
一种混凝土密封固化剂及其施工工艺
WANG XIAODONG (author) / WANG JINLOU (author)
2020-08-14
Patent
Electronic Resource
Chinese
Concrete sealing curing agent and preparation method thereof
European Patent Office | 2021
Concrete sealing curing agent and preparation method thereof
| European Patent Office | 2024
Asphalt pavement sealing compact reduction curing agent and construction process thereof
| European Patent Office | 2021
Concrete sealing curing agent epoxy self-leveling ground construction method
| European Patent Office | 2021